Influence of the strain rate on deformation mechanisms of an AZ31 magnesium alloy
Identifikátory výsledku
Kód výsledku v IS VaVaI
<a href="https://www.isvavai.cz/riv?ss=detail&h=RIV%2F00216208%3A11320%2F13%3A10193127" target="_blank" >RIV/00216208:11320/13:10193127 - isvavai.cz</a>
Výsledek na webu
<a href="http://dx.doi.org/10.3139/146.110922" target="_blank" >http://dx.doi.org/10.3139/146.110922</a>
DOI - Digital Object Identifier
<a href="http://dx.doi.org/10.3139/146.110922" target="_blank" >10.3139/146.110922</a>
Alternativní jazyky
Jazyk výsledku
angličtina
Název v původním jazyce
Influence of the strain rate on deformation mechanisms of an AZ31 magnesium alloy
Popis výsledku v původním jazyce
The paper reports mechanical properties of magnesium alloy AZ31 deformed at low and high strain rates. Material was prepared using squeeze casting technology. Compression tests were performed at an initial strain rate of 8.3 x 10(-5) s(-1) at temperatures between room temperature and 300 degrees C. Dynamic compression Hopkinson tests were carried out at room temperature with impact velocities ranging from 11.2 to 21.9 m s(-1). Transmission electron microscopy investigations showed significant dislocation and twins densities. Results are discussed considering the importance of the activation volume determined in the stress relaxation tests obtained at the low strain rate and, quite separately, the importance of adiabatic shear banding at high strain rates.
Název v anglickém jazyce
Influence of the strain rate on deformation mechanisms of an AZ31 magnesium alloy
Popis výsledku anglicky
The paper reports mechanical properties of magnesium alloy AZ31 deformed at low and high strain rates. Material was prepared using squeeze casting technology. Compression tests were performed at an initial strain rate of 8.3 x 10(-5) s(-1) at temperatures between room temperature and 300 degrees C. Dynamic compression Hopkinson tests were carried out at room temperature with impact velocities ranging from 11.2 to 21.9 m s(-1). Transmission electron microscopy investigations showed significant dislocation and twins densities. Results are discussed considering the importance of the activation volume determined in the stress relaxation tests obtained at the low strain rate and, quite separately, the importance of adiabatic shear banding at high strain rates.
Klasifikace
Druh
J<sub>x</sub> - Nezařazeno - Článek v odborném periodiku (Jimp, Jsc a Jost)
CEP obor
BM - Fyzika pevných látek a magnetismus
OECD FORD obor
—
Návaznosti výsledku
Projekt
<a href="/cs/project/GAP204%2F12%2F1360" target="_blank" >GAP204/12/1360: In-situ výzkum vlivu legovacích prvků na procesy plastické deformace hořčíkových slitin</a><br>
Návaznosti
I - Institucionalni podpora na dlouhodoby koncepcni rozvoj vyzkumne organizace
Ostatní
Rok uplatnění
2013
Kód důvěrnosti údajů
S - Úplné a pravdivé údaje o projektu nepodléhají ochraně podle zvláštních právních předpisů
Údaje specifické pro druh výsledku
Název periodika
International Journal of Materials Research
ISSN
1862-5282
e-ISSN
—
Svazek periodika
104
Číslo periodika v rámci svazku
8
Stát vydavatele periodika
DE - Spolková republika Německo
Počet stran výsledku
7
Strana od-do
762-768
Kód UT WoS článku
000327366400005
EID výsledku v databázi Scopus
—