AGEING STUDY OF TIMETAL LCB TITANIUM ALLOY
Identifikátory výsledku
Kód výsledku v IS VaVaI
<a href="https://www.isvavai.cz/riv?ss=detail&h=RIV%2F00216208%3A11320%2F13%3A10290119" target="_blank" >RIV/00216208:11320/13:10290119 - isvavai.cz</a>
Výsledek na webu
—
DOI - Digital Object Identifier
—
Alternativní jazyky
Jazyk výsledku
angličtina
Název v původním jazyce
AGEING STUDY OF TIMETAL LCB TITANIUM ALLOY
Popis výsledku v původním jazyce
Phase transformations in TIMETAL LCB and their influence on mechanical properties were studied in this research. The ageing response of this material was studied by low temperature ageing at 400, 450 and 500 degrees C. The evolution of volume fractions of alpha, beta and omega phases during ageing was studied by X-ray diffraction (XRD). Mechanical properties were investigated using microhardness measurements and tensile tests. It has been proved that metastable omega phase is formed during annealing at400 and 450 degrees C. omega particles further transform to very fine precipitates of a phase when exposed to annealing for longer time periods. These fine precipitates significantly contribute to increase of microhardness and achieving high value of yield stress.
Název v anglickém jazyce
AGEING STUDY OF TIMETAL LCB TITANIUM ALLOY
Popis výsledku anglicky
Phase transformations in TIMETAL LCB and their influence on mechanical properties were studied in this research. The ageing response of this material was studied by low temperature ageing at 400, 450 and 500 degrees C. The evolution of volume fractions of alpha, beta and omega phases during ageing was studied by X-ray diffraction (XRD). Mechanical properties were investigated using microhardness measurements and tensile tests. It has been proved that metastable omega phase is formed during annealing at400 and 450 degrees C. omega particles further transform to very fine precipitates of a phase when exposed to annealing for longer time periods. These fine precipitates significantly contribute to increase of microhardness and achieving high value of yield stress.
Klasifikace
Druh
D - Stať ve sborníku
CEP obor
BM - Fyzika pevných látek a magnetismus
OECD FORD obor
—
Návaznosti výsledku
Projekt
Výsledek vznikl pri realizaci vícero projektů. Více informací v záložce Projekty.
Návaznosti
P - Projekt vyzkumu a vyvoje financovany z verejnych zdroju (s odkazem do CEP)<br>I - Institucionalni podpora na dlouhodoby koncepcni rozvoj vyzkumne organizace
Ostatní
Rok uplatnění
2013
Kód důvěrnosti údajů
S - Úplné a pravdivé údaje o projektu nepodléhají ochraně podle zvláštních právních předpisů
Údaje specifické pro druh výsledku
Název statě ve sborníku
METAL 2013: 22ND INTERNATIONAL CONFERENCE ON METALLURGY AND MATERIALS
ISBN
978-80-87294-41-3
ISSN
—
e-ISSN
—
Počet stran výsledku
6
Strana od-do
1592-1596
Název nakladatele
TANGER LTD
Místo vydání
SLEZSKA
Místo konání akce
Brno
Datum konání akce
15. 5. 2013
Typ akce podle státní příslušnosti
WRD - Celosvětová akce
Kód UT WoS článku
000333163100264