Hydrogen activation on Pt-Sn nanoalloys supported on mixed Sn-Ce oxide films
Identifikátory výsledku
Kód výsledku v IS VaVaI
<a href="https://www.isvavai.cz/riv?ss=detail&h=RIV%2F00216208%3A11320%2F14%3A10288991" target="_blank" >RIV/00216208:11320/14:10288991 - isvavai.cz</a>
Výsledek na webu
<a href="http://dx.doi.org/10.1039/c4cp01632g" target="_blank" >http://dx.doi.org/10.1039/c4cp01632g</a>
DOI - Digital Object Identifier
<a href="http://dx.doi.org/10.1039/c4cp01632g" target="_blank" >10.1039/c4cp01632g</a>
Alternativní jazyky
Jazyk výsledku
angličtina
Název v původním jazyce
Hydrogen activation on Pt-Sn nanoalloys supported on mixed Sn-Ce oxide films
Popis výsledku v původním jazyce
We have studied the interaction of H-2 with Pt-Sn nanoalloys supported on Sn-Ce mixed oxide films of different composition by means of synchrotron radiation photoelectron spectroscopy and resonant photoemission spectroscopy. The model catalysts are prepared in a three step procedure that involves (i) the preparation of well-ordered CeO2(111) films on Cu(111) followed by subsequent physical vapor deposition of (ii) metallic Sn and (iii) metallic Pt. The formation of mixed Sn-Ce oxide is accompanied by partial reduction of Ce4+ cations to Ce3+. Pt deposition leads to the formation of Pt-Sn nanoalloys accompanied by the partial re-oxidation of Ce3+ to Ce4+. Subsequent annealing promotes further Pt-Sn alloy formation at expense of the Sn content in the Sn-Ce mixed oxide. Adsorption of H-2 on Pt-Sn/Sn-Ce-O at 150 K followed by stepwise annealing results in reversible reduction of Ce cations caused by spillover of dissociated hydrogen between 150 and 300 K. Above 500 K, annealing of Pt-Sn/Sn
Název v anglickém jazyce
Hydrogen activation on Pt-Sn nanoalloys supported on mixed Sn-Ce oxide films
Popis výsledku anglicky
We have studied the interaction of H-2 with Pt-Sn nanoalloys supported on Sn-Ce mixed oxide films of different composition by means of synchrotron radiation photoelectron spectroscopy and resonant photoemission spectroscopy. The model catalysts are prepared in a three step procedure that involves (i) the preparation of well-ordered CeO2(111) films on Cu(111) followed by subsequent physical vapor deposition of (ii) metallic Sn and (iii) metallic Pt. The formation of mixed Sn-Ce oxide is accompanied by partial reduction of Ce4+ cations to Ce3+. Pt deposition leads to the formation of Pt-Sn nanoalloys accompanied by the partial re-oxidation of Ce3+ to Ce4+. Subsequent annealing promotes further Pt-Sn alloy formation at expense of the Sn content in the Sn-Ce mixed oxide. Adsorption of H-2 on Pt-Sn/Sn-Ce-O at 150 K followed by stepwise annealing results in reversible reduction of Ce cations caused by spillover of dissociated hydrogen between 150 and 300 K. Above 500 K, annealing of Pt-Sn/Sn
Klasifikace
Druh
J<sub>x</sub> - Nezařazeno - Článek v odborném periodiku (Jimp, Jsc a Jost)
CEP obor
BM - Fyzika pevných látek a magnetismus
OECD FORD obor
—
Návaznosti výsledku
Projekt
Výsledek vznikl pri realizaci vícero projektů. Více informací v záložce Projekty.
Návaznosti
P - Projekt vyzkumu a vyvoje financovany z verejnych zdroju (s odkazem do CEP)<br>I - Institucionalni podpora na dlouhodoby koncepcni rozvoj vyzkumne organizace
Ostatní
Rok uplatnění
2014
Kód důvěrnosti údajů
S - Úplné a pravdivé údaje o projektu nepodléhají ochraně podle zvláštních právních předpisů
Údaje specifické pro druh výsledku
Název periodika
Physical Chemistry Chemical Physics
ISSN
1463-9076
e-ISSN
—
Svazek periodika
16
Číslo periodika v rámci svazku
26
Stát vydavatele periodika
GB - Spojené království Velké Británie a Severního Irska
Počet stran výsledku
8
Strana od-do
13209-13219
Kód UT WoS článku
000337785400024
EID výsledku v databázi Scopus
—