Planar defects in magnesium alloys

Kód výsledku v IS VaVaI

<a href="https://www.isvavai.cz/riv?ss=detail&h=RIV%2F00216208%3A11320%2F15%3A10315939" target="_blank" >RIV/00216208:11320/15:10315939 - isvavai.cz</a>

Výsledek na webu

<a href="http://www.ecmjournal.org/journal/supplements/vol030supp03/vol030supp03.htm" target="_blank" >http://www.ecmjournal.org/journal/supplements/vol030supp03/vol030supp03.htm</a>

DOI - Digital Object Identifier

—

Jazyk výsledku

angličtina

Název v původním jazyce

Planar defects in magnesium alloys

Popis výsledku v původním jazyce

Metastable phases in form of planar defects are responsible for the top strength in many Mg alloys, especially with rare earth elements (RE) (Y included) and affect their corrosion. Orientation of these defects in the ?-Mg matrix determines strictly their hardening effect. Peak hardening in Mg-RE alloys is reached by dense triangular arrangement of prismatic plates, whereas basal plates have only a moderate effect on basal dislocations slip. The Zn addition in the alloys leads to a decrease of stackingfault (SF) energy and consequently to formation of variety of thin basal planar defects. Moreover, Zn addition was proved to favourably influence corrosion and biocompatibility of some of these alloys (e.g. Mg2Y1Zn in wt. %).

Název v anglickém jazyce

Planar defects in magnesium alloys

Popis výsledku anglicky

Metastable phases in form of planar defects are responsible for the top strength in many Mg alloys, especially with rare earth elements (RE) (Y included) and affect their corrosion. Orientation of these defects in the ?-Mg matrix determines strictly their hardening effect. Peak hardening in Mg-RE alloys is reached by dense triangular arrangement of prismatic plates, whereas basal plates have only a moderate effect on basal dislocations slip. The Zn addition in the alloys leads to a decrease of stackingfault (SF) energy and consequently to formation of variety of thin basal planar defects. Moreover, Zn addition was proved to favourably influence corrosion and biocompatibility of some of these alloys (e.g. Mg2Y1Zn in wt. %).

Druh

J_x - Nezařazeno - Článek v odborném periodiku (Jimp, Jsc a Jost)

CEP obor

JG - Hutnictví, kovové materiály

OECD FORD obor

—

Projekt

—

Návaznosti

R - Projekt Ramcoveho programu EK

Rok uplatnění

2015

Kód důvěrnosti údajů

S - Úplné a pravdivé údaje o projektu nepodléhají ochraně podle zvláštních právních předpisů

Název periodika

European Cells and Materials

ISSN

1473-2262

e-ISSN

—

Svazek periodika

30

Číslo periodika v rámci svazku

Suppl. 3

Stát vydavatele periodika

CH - Švýcarská konfederace

Počet stran výsledku

1

Strana od-do

24

Kód UT WoS článku

—

EID výsledku v databázi Scopus

—