Magneto-optical studies of BaFe12O19 films grown by metallo-organic decomposition

Kód výsledku v IS VaVaI

<a href="https://www.isvavai.cz/riv?ss=detail&h=RIV%2F00216208%3A11320%2F15%3A10316851" target="_blank" >RIV/00216208:11320/15:10316851 - isvavai.cz</a>

Nalezeny alternativní kódy

RIV/61989100:27640/15:86095467

Výsledek na webu

<a href="http://dx.doi.org/10.1364/OME.5.001323" target="_blank" >http://dx.doi.org/10.1364/OME.5.001323</a>

DOI - Digital Object Identifier

<a href="http://dx.doi.org/10.1364/OME.5.001323" target="_blank" >10.1364/OME.5.001323</a>

Jazyk výsledku

angličtina

Název v původním jazyce

Magneto-optical studies of BaFe12O19 films grown by metallo-organic decomposition

Popis výsledku v původním jazyce

M-type barium hexagonal ferrites BaFe12O19 (BaM) films considered for new devices that operate in the 40-70 GHz range with small or zero applied magnetic fields were characterized by magneto-optical (MO) complex polar "Kerr" effect (PKE) spectroscopy, MOmagnetometry, and spectral ellipsometry (SE). The textured polycrystalline films were grown on Pt(111)/TiO2 template on Si wafer using metallo-organic decomposition technique (MOD) followed by rapid thermal annealing. In the films grown in one, two andthree MOD iterations, the thickness was evaluated by SE and transmission electron microscopy. The film thickness ranged from 30 nm to 50 nm per MOD iteration. The best films display out-of-plane effective magnetic anisotropy field of 13 kOe, high perpendicular remanent magnetization and ferromagnetic resonance linewidth of 340 Oe at 60 GHz. The coercivity deduced from the MO hysteresis loops ranged between 0.25 kOe and 0.52 kOe. The SE and PKE spectra were taken at photon energies from 0

Název v anglickém jazyce

Magneto-optical studies of BaFe12O19 films grown by metallo-organic decomposition

Popis výsledku anglicky

M-type barium hexagonal ferrites BaFe12O19 (BaM) films considered for new devices that operate in the 40-70 GHz range with small or zero applied magnetic fields were characterized by magneto-optical (MO) complex polar "Kerr" effect (PKE) spectroscopy, MOmagnetometry, and spectral ellipsometry (SE). The textured polycrystalline films were grown on Pt(111)/TiO2 template on Si wafer using metallo-organic decomposition technique (MOD) followed by rapid thermal annealing. In the films grown in one, two andthree MOD iterations, the thickness was evaluated by SE and transmission electron microscopy. The film thickness ranged from 30 nm to 50 nm per MOD iteration. The best films display out-of-plane effective magnetic anisotropy field of 13 kOe, high perpendicular remanent magnetization and ferromagnetic resonance linewidth of 340 Oe at 60 GHz. The coercivity deduced from the MO hysteresis loops ranged between 0.25 kOe and 0.52 kOe. The SE and PKE spectra were taken at photon energies from 0

Druh

J_x - Nezařazeno - Článek v odborném periodiku (Jimp, Jsc a Jost)

CEP obor

BM - Fyzika pevných látek a magnetismus

OECD FORD obor

—

Projekt

Výsledek vznikl pri realizaci vícero projektů. Více informací v záložce Projekty.

Návaznosti

I - Institucionalni podpora na dlouhodoby koncepcni rozvoj vyzkumne organizace

Rok uplatnění

2015

Kód důvěrnosti údajů

S - Úplné a pravdivé údaje o projektu nepodléhají ochraně podle zvláštních právních předpisů

Název periodika

Optical Materials Express

ISSN

2159-3930

e-ISSN

—

Svazek periodika

5

Číslo periodika v rámci svazku

6

Stát vydavatele periodika

US - Spojené státy americké

Počet stran výsledku

8

Strana od-do

1323-1330

Kód UT WoS článku

000355627100010

EID výsledku v databázi Scopus

2-s2.0-84947596397