Texture analysis of zirconium samples deformed by uniaxial tension using neutron and X-ray diffraction

Kód výsledku v IS VaVaI

<a href="https://www.isvavai.cz/riv?ss=detail&h=RIV%2F00216208%3A11320%2F15%3A10317614" target="_blank" >RIV/00216208:11320/15:10317614 - isvavai.cz</a>

Nalezeny alternativní kódy

RIV/68407700:21340/15:00235897

Výsledek na webu

<a href="http://dx.doi.org/10.1088/1757-899X/82/1/012022" target="_blank" >http://dx.doi.org/10.1088/1757-899X/82/1/012022</a>

DOI - Digital Object Identifier

<a href="http://dx.doi.org/10.1088/1757-899X/82/1/012022" target="_blank" >10.1088/1757-899X/82/1/012022</a>

Jazyk výsledku

angličtina

Název v původním jazyce

Texture analysis of zirconium samples deformed by uniaxial tension using neutron and X-ray diffraction

Popis výsledku v původním jazyce

Seven zirconium samples were studied by neutron and X-ray diffraction after deformation on uniaxial tensile machine INSTRON 5882 from strain 5% to strain 30% (strain step was 5%). Preferred orientation parameters were determined by using pole figures andinverse pole figures. The X-ray measurements were performed at theta/theta X'Pert PRO diffractometer with Cr X-ray tube. Observed data were processed by software packages GSAS and X'Pert Texture. Our results can be summarized as follows: (i) Samples prefer orientation of planes (100) and (110) perpendicular to rolling direction. (ii) The position of the basal poles is tilted by 30 degrees from the normal direction toward the transverse direction. (iii) Samples prefer orientation of planes (102) and (103) perpendicular to normal direction. (iv) Level of resulting texture increases with deformation. The obtained results are characteristic for zirconium.

Název v anglickém jazyce

Texture analysis of zirconium samples deformed by uniaxial tension using neutron and X-ray diffraction

Popis výsledku anglicky

Seven zirconium samples were studied by neutron and X-ray diffraction after deformation on uniaxial tensile machine INSTRON 5882 from strain 5% to strain 30% (strain step was 5%). Preferred orientation parameters were determined by using pole figures andinverse pole figures. The X-ray measurements were performed at theta/theta X'Pert PRO diffractometer with Cr X-ray tube. Observed data were processed by software packages GSAS and X'Pert Texture. Our results can be summarized as follows: (i) Samples prefer orientation of planes (100) and (110) perpendicular to rolling direction. (ii) The position of the basal poles is tilted by 30 degrees from the normal direction toward the transverse direction. (iii) Samples prefer orientation of planes (102) and (103) perpendicular to normal direction. (iv) Level of resulting texture increases with deformation. The obtained results are characteristic for zirconium.

Druh

D - Stať ve sborníku

CEP obor

BM - Fyzika pevných látek a magnetismus

OECD FORD obor

—

Projekt

<a href="/cs/project/GB14-36566G" target="_blank" >GB14-36566G: Multidisciplinární výzkumné centrum moderních materiálů</a><br>

Návaznosti

I - Institucionalni podpora na dlouhodoby koncepcni rozvoj vyzkumne organizace

Rok uplatnění

2015

Kód důvěrnosti údajů

S - Úplné a pravdivé údaje o projektu nepodléhají ochraně podle zvláštních právních předpisů

Název statě ve sborníku

IOP Conference Series: Materials Science and Engineering

ISBN

—

ISSN

1757-8981

e-ISSN

—

Počet stran výsledku

5

Strana od-do

—

Název nakladatele

IOP PUBLISHING LTD

Místo vydání

BRISTOL

Místo konání akce

Dresden

Datum konání akce

24. 8. 2014

Typ akce podle státní příslušnosti

WRD - Celosvětová akce

Kód UT WoS článku

000354878500023