Evolution of Corrosion Resistance in the LAE442 Magnesium Alloy Processed by ECAP
Identifikátory výsledku
Kód výsledku v IS VaVaI
<a href="https://www.isvavai.cz/riv?ss=detail&h=RIV%2F00216208%3A11320%2F15%3A10318003" target="_blank" >RIV/00216208:11320/15:10318003 - isvavai.cz</a>
Výsledek na webu
<a href="http://dx.doi.org/10.12693/APhysPolA.128.772" target="_blank" >http://dx.doi.org/10.12693/APhysPolA.128.772</a>
DOI - Digital Object Identifier
<a href="http://dx.doi.org/10.12693/APhysPolA.128.772" target="_blank" >10.12693/APhysPolA.128.772</a>
Alternativní jazyky
Jazyk výsledku
angličtina
Název v původním jazyce
Evolution of Corrosion Resistance in the LAE442 Magnesium Alloy Processed by ECAP
Popis výsledku v původním jazyce
The influence of processing by equal channel angular pressing on the corrosion resistance was investigated in the extruded LAE442 magnesium alloy by the linear polarization method. Continuous increase of the corrosion resistance with the increasing number of passes was measured. The polarization resistance of the 12P sample was substantially higher as compared to the extruded state. The results were discussed in terms of the corrosion layers formed on the surface after seven days of immersion. It was concluded that the substantial increase of polarization resistance was caused by the combined effect of grain refinement and aluminum and lithium oxides formation within the corrosion layer.
Název v anglickém jazyce
Evolution of Corrosion Resistance in the LAE442 Magnesium Alloy Processed by ECAP
Popis výsledku anglicky
The influence of processing by equal channel angular pressing on the corrosion resistance was investigated in the extruded LAE442 magnesium alloy by the linear polarization method. Continuous increase of the corrosion resistance with the increasing number of passes was measured. The polarization resistance of the 12P sample was substantially higher as compared to the extruded state. The results were discussed in terms of the corrosion layers formed on the surface after seven days of immersion. It was concluded that the substantial increase of polarization resistance was caused by the combined effect of grain refinement and aluminum and lithium oxides formation within the corrosion layer.
Klasifikace
Druh
J<sub>x</sub> - Nezařazeno - Článek v odborném periodiku (Jimp, Jsc a Jost)
CEP obor
BM - Fyzika pevných látek a magnetismus
OECD FORD obor
—
Návaznosti výsledku
Projekt
Výsledek vznikl pri realizaci vícero projektů. Více informací v záložce Projekty.
Návaznosti
P - Projekt vyzkumu a vyvoje financovany z verejnych zdroju (s odkazem do CEP)<br>I - Institucionalni podpora na dlouhodoby koncepcni rozvoj vyzkumne organizace
Ostatní
Rok uplatnění
2015
Kód důvěrnosti údajů
S - Úplné a pravdivé údaje o projektu nepodléhají ochraně podle zvláštních právních předpisů
Údaje specifické pro druh výsledku
Název periodika
Acta Physica Polonica A
ISSN
0587-4246
e-ISSN
—
Svazek periodika
128
Číslo periodika v rámci svazku
4
Stát vydavatele periodika
PL - Polská republika
Počet stran výsledku
3
Strana od-do
772-774
Kód UT WoS článku
000366357300074
EID výsledku v databázi Scopus
2-s2.0-84950268151