The investigation of Al7075 and Al7075+1wt.% Zr alloys prepared by spark plasma sintering technology
Identifikátory výsledku
Kód výsledku v IS VaVaI
<a href="https://www.isvavai.cz/riv?ss=detail&h=RIV%2F00216208%3A11320%2F15%3A10318556" target="_blank" >RIV/00216208:11320/15:10318556 - isvavai.cz</a>
Výsledek na webu
—
DOI - Digital Object Identifier
—
Alternativní jazyky
Jazyk výsledku
angličtina
Název v původním jazyce
The investigation of Al7075 and Al7075+1wt.% Zr alloys prepared by spark plasma sintering technology
Popis výsledku v původním jazyce
The development of high strength materials with sufficient deformability requires new processing routes. Powders with fine grain structure and special phase composition can be prepared by powder metallurgy. Spark plasma sintering (SPS) enables the conservation of such microstructure in the compact material. Compacts of aluminium alloys were prepared by SPS (500 oC for 3 min) of gas atomised powders. The grain structure remained unchanged during SPS, but significant changes in the distribution of phaseswere observed by scanning electron microscopy. The microhardness of sintered samples was measured after thermal treatments. The grain size remained unchanged during annealing at even 500 oC for 10 hours, but the materials' microhardness changed significantly as a result of changes in the phase composition. The materials exhibited both artificial and natural ageing.
Název v anglickém jazyce
The investigation of Al7075 and Al7075+1wt.% Zr alloys prepared by spark plasma sintering technology
Popis výsledku anglicky
The development of high strength materials with sufficient deformability requires new processing routes. Powders with fine grain structure and special phase composition can be prepared by powder metallurgy. Spark plasma sintering (SPS) enables the conservation of such microstructure in the compact material. Compacts of aluminium alloys were prepared by SPS (500 oC for 3 min) of gas atomised powders. The grain structure remained unchanged during SPS, but significant changes in the distribution of phaseswere observed by scanning electron microscopy. The microhardness of sintered samples was measured after thermal treatments. The grain size remained unchanged during annealing at even 500 oC for 10 hours, but the materials' microhardness changed significantly as a result of changes in the phase composition. The materials exhibited both artificial and natural ageing.
Klasifikace
Druh
D - Stať ve sborníku
CEP obor
BM - Fyzika pevných látek a magnetismus
OECD FORD obor
—
Návaznosti výsledku
Projekt
<a href="/cs/project/GA15-15609S" target="_blank" >GA15-15609S: Ultra-jemnozrnné a nanokrystalické kovové materiály s vysokou pevností připravené slinovaním pulzním elektrickým proudem</a><br>
Návaznosti
S - Specificky vyzkum na vysokych skolach<br>I - Institucionalni podpora na dlouhodoby koncepcni rozvoj vyzkumne organizace
Ostatní
Rok uplatnění
2015
Kód důvěrnosti údajů
S - Úplné a pravdivé údaje o projektu nepodléhají ochraně podle zvláštních právních předpisů
Údaje specifické pro druh výsledku
Název statě ve sborníku
WDS'15 Proceedings of Contributed Papers - Physics
ISBN
978-80-7378-311-2
ISSN
—
e-ISSN
—
Počet stran výsledku
6
Strana od-do
61-66
Název nakladatele
Matfyzpress
Místo vydání
Praha
Místo konání akce
Prague, Czech Republic
Datum konání akce
2. 6. 2015
Typ akce podle státní příslušnosti
CST - Celostátní akce
Kód UT WoS článku
—