Monitoring the failure mechanisms in metal matrix syntactic foams during compression by acoustic emission

Kód výsledku v IS VaVaI

<a href="https://www.isvavai.cz/riv?ss=detail&h=RIV%2F00216208%3A11320%2F16%3A10334809" target="_blank" >RIV/00216208:11320/16:10334809 - isvavai.cz</a>

Výsledek na webu

<a href="http://dx.doi.org/10.1016/j.matlet.2016.02.102" target="_blank" >http://dx.doi.org/10.1016/j.matlet.2016.02.102</a>

DOI - Digital Object Identifier

<a href="http://dx.doi.org/10.1016/j.matlet.2016.02.102" target="_blank" >10.1016/j.matlet.2016.02.102</a>

Jazyk výsledku

angličtina

Název v původním jazyce

Monitoring the failure mechanisms in metal matrix syntactic foams during compression by acoustic emission

Popis výsledku v původním jazyce

Syntactic foam containing hollow ceramic spheres with an average outer diameter of 1.45 mm and wall thickness of 58 tm was produced using the pressure infiltration technique. This paper presents the analysis of the compressive deformation mechanisms of these syntactic foams using the acoustic emission (AE) technique. The active deformation mechanisms are determined by sequential k -means analysis of the AE data. The analysis revealed three dominant deformation mechanisms: plastic deformation of the cell walls, sphere fracture, and cell wall collapse. The AE results obtained are in good correlation with the findings of the visual inspection of the surface of the specimen, suggesting that the active deformation mechanisms in the whole volume of the specimen can be determined by this technique.

Název v anglickém jazyce

Monitoring the failure mechanisms in metal matrix syntactic foams during compression by acoustic emission

Popis výsledku anglicky

Syntactic foam containing hollow ceramic spheres with an average outer diameter of 1.45 mm and wall thickness of 58 tm was produced using the pressure infiltration technique. This paper presents the analysis of the compressive deformation mechanisms of these syntactic foams using the acoustic emission (AE) technique. The active deformation mechanisms are determined by sequential k -means analysis of the AE data. The analysis revealed three dominant deformation mechanisms: plastic deformation of the cell walls, sphere fracture, and cell wall collapse. The AE results obtained are in good correlation with the findings of the visual inspection of the surface of the specimen, suggesting that the active deformation mechanisms in the whole volume of the specimen can be determined by this technique.

Druh

J_x - Nezařazeno - Článek v odborném periodiku (Jimp, Jsc a Jost)

CEP obor

BM - Fyzika pevných látek a magnetismus

OECD FORD obor

—

Projekt

<a href="/cs/project/GA15-10821S" target="_blank" >GA15-10821S: Velikostní efekt při plastické deformaci materiálů</a><br>

Návaznosti

P - Projekt vyzkumu a vyvoje financovany z verejnych zdroju (s odkazem do CEP)

Rok uplatnění

2016

Kód důvěrnosti údajů

S - Úplné a pravdivé údaje o projektu nepodléhají ochraně podle zvláštních právních předpisů

Název periodika

Materials Letters

ISSN

0167-577X

e-ISSN

—

Svazek periodika

173

Číslo periodika v rámci svazku

-

Stát vydavatele periodika

NL - Nizozemsko

Počet stran výsledku

4

Strana od-do

31-34

Kód UT WoS článku

000374325900008

EID výsledku v databázi Scopus

2-s2.0-84960153140