Secondary phase precipitation and thermally stable microstructure refinement induced by ECAP on Mg-Y-Nd (WN43) alloy

Kód výsledku v IS VaVaI

<a href="https://www.isvavai.cz/riv?ss=detail&h=RIV%2F00216208%3A11320%2F19%3A10388988" target="_blank" >RIV/00216208:11320/19:10388988 - isvavai.cz</a>

Výsledek na webu

<a href="https://verso.is.cuni.cz/pub/verso.fpl?fname=obd_publikace_handle&handle=jOBb4Dc59r" target="_blank" >https://verso.is.cuni.cz/pub/verso.fpl?fname=obd_publikace_handle&handle=jOBb4Dc59r</a>

DOI - Digital Object Identifier

<a href="http://dx.doi.org/10.1016/j.matlet.2018.09.107" target="_blank" >10.1016/j.matlet.2018.09.107</a>

Jazyk výsledku

angličtina

Název v původním jazyce

Secondary phase precipitation and thermally stable microstructure refinement induced by ECAP on Mg-Y-Nd (WN43) alloy

Popis výsledku v původním jazyce

Magnesium alloy Mg-4Y-3Nd (WN43) was subjected to ECAP at T similar to 300 degrees C up to 8 passes, using route B-C. The initial as-extruded material with average grain size of similar to 10 mu m, was effectively refined down to sub-micrometer scale, reaching a grain size of similar to 380 nm, after 8 passes. At the same time, secondary phase particle precipitation of beta&apos;-Mg12Nd2Y, and beta-Mg14Nd2Y was induced. At 8 passes, fragmentation and coarsening of these phases occurred. Both grain refinement and beta&apos;/beta precipitation strengthened the alloy. The strengthening was detected by nanoindentation hardness and accounted of up to 30% increment at 8 ECAP pass, compared to the initial extruded condition. (C) 2018 Elsevier B.V. All rights reserved.

Název v anglickém jazyce

Secondary phase precipitation and thermally stable microstructure refinement induced by ECAP on Mg-Y-Nd (WN43) alloy

Popis výsledku anglicky

Magnesium alloy Mg-4Y-3Nd (WN43) was subjected to ECAP at T similar to 300 degrees C up to 8 passes, using route B-C. The initial as-extruded material with average grain size of similar to 10 mu m, was effectively refined down to sub-micrometer scale, reaching a grain size of similar to 380 nm, after 8 passes. At the same time, secondary phase particle precipitation of beta&apos;-Mg12Nd2Y, and beta-Mg14Nd2Y was induced. At 8 passes, fragmentation and coarsening of these phases occurred. Both grain refinement and beta&apos;/beta precipitation strengthened the alloy. The strengthening was detected by nanoindentation hardness and accounted of up to 30% increment at 8 ECAP pass, compared to the initial extruded condition. (C) 2018 Elsevier B.V. All rights reserved.

Druh

J_imp - Článek v periodiku v databázi Web of Science

CEP obor

—

OECD FORD obor

10302 - Condensed matter physics (including formerly solid state physics, supercond.)

Projekt

<a href="/cs/project/GB14-36566G" target="_blank" >GB14-36566G: Multidisciplinární výzkumné centrum moderních materiálů</a><br>

Návaznosti

P - Projekt vyzkumu a vyvoje financovany z verejnych zdroju (s odkazem do CEP)

Rok uplatnění

2019

Kód důvěrnosti údajů

S - Úplné a pravdivé údaje o projektu nepodléhají ochraně podle zvláštních právních předpisů

Název periodika

Materials Letters

ISSN

0167-577X

e-ISSN

—

Svazek periodika

237

Číslo periodika v rámci svazku

1

Stát vydavatele periodika

NL - Nizozemsko

Počet stran výsledku

4

Strana od-do

5-8

Kód UT WoS článku

000454609700002

EID výsledku v databázi Scopus

2-s2.0-85056463281