Microstructure evolution and mechanical behaviour of severely deformed pure titanium through multi directional forging
Identifikátory výsledku
Kód výsledku v IS VaVaI
<a href="https://www.isvavai.cz/riv?ss=detail&h=RIV%2F00216208%3A11320%2F19%3A10405719" target="_blank" >RIV/00216208:11320/19:10405719 - isvavai.cz</a>
Výsledek na webu
<a href="https://verso.is.cuni.cz/pub/verso.fpl?fname=obd_publikace_handle&handle=D_9S1eBFYz" target="_blank" >https://verso.is.cuni.cz/pub/verso.fpl?fname=obd_publikace_handle&handle=D_9S1eBFYz</a>
DOI - Digital Object Identifier
<a href="http://dx.doi.org/10.1016/j.jallcom.2018.10.196" target="_blank" >10.1016/j.jallcom.2018.10.196</a>
Alternativní jazyky
Jazyk výsledku
angličtina
Název v původním jazyce
Microstructure evolution and mechanical behaviour of severely deformed pure titanium through multi directional forging
Popis výsledku v původním jazyce
Multi directional forging (MDF) is one of the severe plastic deformation methods utilized for production of ultrafine grained materials with improved mechanical properties. The main goal of the current study is to enhance mechanical properties of commercial pure (CP) titanium using grain refinement by MDF method. For this purpose, after one hour annealing at 800 degrees C, the CP titanium was forged by MDF process up to six passes at room and 220 degrees C temperatures. The results of microstructure analysis by scanning electron microscope equipped with EBSD showed that average grain size of samples after six MDF passes at room and 220 degrees C temperatures was about 60 times finer than that of the annealed specimen. The mean grain size of the titanium is reduced from 64 mu m to 1 mu m after 6 passes at room temperature. Also, the tensile and shear strengths are notably improved by increasing number of MDF passes and reduction of the processing temperature. Yield tensile and shear strengths of six passes MDFed samples at room temperature were about 2.5 times greater than those of the annealed specimen. The correlation between tensile and shear strengths was studied as well. The ratio between yield tensile and shear strengths and also between ultimate tensile and shear strengths was achieved about 1.5 and 2, respectively. (C) 2018 Elsevier B.V. All rights reserved.
Název v anglickém jazyce
Microstructure evolution and mechanical behaviour of severely deformed pure titanium through multi directional forging
Popis výsledku anglicky
Multi directional forging (MDF) is one of the severe plastic deformation methods utilized for production of ultrafine grained materials with improved mechanical properties. The main goal of the current study is to enhance mechanical properties of commercial pure (CP) titanium using grain refinement by MDF method. For this purpose, after one hour annealing at 800 degrees C, the CP titanium was forged by MDF process up to six passes at room and 220 degrees C temperatures. The results of microstructure analysis by scanning electron microscope equipped with EBSD showed that average grain size of samples after six MDF passes at room and 220 degrees C temperatures was about 60 times finer than that of the annealed specimen. The mean grain size of the titanium is reduced from 64 mu m to 1 mu m after 6 passes at room temperature. Also, the tensile and shear strengths are notably improved by increasing number of MDF passes and reduction of the processing temperature. Yield tensile and shear strengths of six passes MDFed samples at room temperature were about 2.5 times greater than those of the annealed specimen. The correlation between tensile and shear strengths was studied as well. The ratio between yield tensile and shear strengths and also between ultimate tensile and shear strengths was achieved about 1.5 and 2, respectively. (C) 2018 Elsevier B.V. All rights reserved.
Klasifikace
Druh
J<sub>imp</sub> - Článek v periodiku v databázi Web of Science
CEP obor
—
OECD FORD obor
10302 - Condensed matter physics (including formerly solid state physics, supercond.)
Návaznosti výsledku
Projekt
<a href="/cs/project/GB14-36566G" target="_blank" >GB14-36566G: Multidisciplinární výzkumné centrum moderních materiálů</a><br>
Návaznosti
P - Projekt vyzkumu a vyvoje financovany z verejnych zdroju (s odkazem do CEP)
Ostatní
Rok uplatnění
2019
Kód důvěrnosti údajů
S - Úplné a pravdivé údaje o projektu nepodléhají ochraně podle zvláštních právních předpisů
Údaje specifické pro druh výsledku
Název periodika
Journal of Alloys and Compounds
ISSN
0925-8388
e-ISSN
—
Svazek periodika
776
Číslo periodika v rámci svazku
1
Stát vydavatele periodika
CH - Švýcarská konfederace
Počet stran výsledku
13
Strana od-do
83-95
Kód UT WoS článku
000453826200011
EID výsledku v databázi Scopus
2-s2.0-85055581681