Long-Term Corrosion Behavior of Biocompatible Beta-Type Ti Alloy in Simulated Body Fuid

Kód výsledku v IS VaVaI

<a href="https://www.isvavai.cz/riv?ss=detail&h=RIV%2F00216224%3A14110%2F12%3A00061744" target="_blank" >RIV/00216224:14110/12:00061744 - isvavai.cz</a>

Výsledek na webu

<a href="http://dx.doi.org/10.1149/2.045210jes" target="_blank" >http://dx.doi.org/10.1149/2.045210jes</a>

DOI - Digital Object Identifier

<a href="http://dx.doi.org/10.1149/2.045210jes" target="_blank" >10.1149/2.045210jes</a>

Jazyk výsledku

angličtina

Název v původním jazyce

Long-Term Corrosion Behavior of Biocompatible Beta-Type Ti Alloy in Simulated Body Fuid

Popis výsledku v původním jazyce

The corrosion behavior of the Ti-33.5Nb-5.7Ta alloy (Ti-Nb-Ta) as a biocompatible Beta-type Ti alloy during long-term immersion in simulated body fluid was investigated. Like pure Ti, pitting corrosion did not occur on Ti-Nb-Ta during anodic polarization. Thus, alloying of Ti with Nb and Ta did not change the chloride-ion sensitivity. Metal ion release of Ti, Nb, and Ta was detected after 7-d immersion in the solution; however, the amounts of ions were much smaller than those from Type316L stainless steel. X-ray photoelectron spectroscopy revealed that the fractions of Nb and Ta in the passive layer increased during the immersion while that of Ti decreased. The corrosion rate of Ti-Nb-Ta determined by electrochemical impedance spectroscopy kept decreasing over a period of 15 d while the thickness of the passive layer did not change after 1 d. Thus, the reconstruction of the passive layer of the alloy was proven to be important for metal ion release during long-term implantation in a li

Název v anglickém jazyce

Long-Term Corrosion Behavior of Biocompatible Beta-Type Ti Alloy in Simulated Body Fuid

Popis výsledku anglicky

The corrosion behavior of the Ti-33.5Nb-5.7Ta alloy (Ti-Nb-Ta) as a biocompatible Beta-type Ti alloy during long-term immersion in simulated body fluid was investigated. Like pure Ti, pitting corrosion did not occur on Ti-Nb-Ta during anodic polarization. Thus, alloying of Ti with Nb and Ta did not change the chloride-ion sensitivity. Metal ion release of Ti, Nb, and Ta was detected after 7-d immersion in the solution; however, the amounts of ions were much smaller than those from Type316L stainless steel. X-ray photoelectron spectroscopy revealed that the fractions of Nb and Ta in the passive layer increased during the immersion while that of Ti decreased. The corrosion rate of Ti-Nb-Ta determined by electrochemical impedance spectroscopy kept decreasing over a period of 15 d while the thickness of the passive layer did not change after 1 d. Thus, the reconstruction of the passive layer of the alloy was proven to be important for metal ion release during long-term implantation in a li

Druh

J_x - Nezařazeno - Článek v odborném periodiku (Jimp, Jsc a Jost)

CEP obor

FF - ORL, oftalmologie, stomatologie

OECD FORD obor

—

Projekt

<a href="/cs/project/1M0528" target="_blank" >1M0528: Stomatologické výzkumné centrum</a><br>

Návaznosti

P - Projekt vyzkumu a vyvoje financovany z verejnych zdroju (s odkazem do CEP)

Rok uplatnění

2012

Kód důvěrnosti údajů

S - Úplné a pravdivé údaje o projektu nepodléhají ochraně podle zvláštních právních předpisů

Název periodika

Journal of the electrochemical society

ISSN

0013-4651

e-ISSN

—

Svazek periodika

159

Číslo periodika v rámci svazku

10

Stát vydavatele periodika

US - Spojené státy americké

Počet stran výsledku

6

Strana od-do

"C435"-"C440"

Kód UT WoS článku

000309105500030

EID výsledku v databázi Scopus

—