Weld joint simulations of heat-resistant steels

Popis výsledku v původním jazyce

Knowledge of microstructure stability is essential for reliable estimations of the lifetime limitations of materials and welded joints at higher temperatures. The CALPHAD method complemented with appropriate diffusion approach can help us to simulate phase and element profile evolutions inside diffusion-affected zone of weld joint. The different heat-resistant steels (alloying base: Cr, Ni, Mo, V, C, N) and their weld joints are objects of our study. The particular results of the equilibrium calculations are presented as phase diagram cross-sections and element activities of the selected heat-resistant steels. The carbon and nitrogen activity temperature dependences were calculated for individual steels. The difference in these activities in two different steels (at given temperature) indicates diffusion flow direction, which can be opposite then deduced from the element content (up-hill diffusion). The simulations respect the coexistence of different carbide phases in the materials an

Název v anglickém jazyce

Weld joint simulations of heat-resistant steels

Popis výsledku anglicky

Knowledge of microstructure stability is essential for reliable estimations of the lifetime limitations of materials and welded joints at higher temperatures. The CALPHAD method complemented with appropriate diffusion approach can help us to simulate phase and element profile evolutions inside diffusion-affected zone of weld joint. The different heat-resistant steels (alloying base: Cr, Ni, Mo, V, C, N) and their weld joints are objects of our study. The particular results of the equilibrium calculations are presented as phase diagram cross-sections and element activities of the selected heat-resistant steels. The carbon and nitrogen activity temperature dependences were calculated for individual steels. The difference in these activities in two different steels (at given temperature) indicates diffusion flow direction, which can be opposite then deduced from the element content (up-hill diffusion). The simulations respect the coexistence of different carbide phases in the materials an

Druh

J_x - Nezařazeno - Článek v odborném periodiku (Jimp, Jsc a Jost)

CEP obor

CF - Fyzikální chemie a teoretická chemie

OECD FORD obor

—

Projekt

<a href="/cs/project/GA106%2F03%2F0636" target="_blank" >GA106/03/0636: Teoretické modelování a experimentální studium strukturní stability moderních žárupevných ocelí a jejich svarů</a><br>

Návaznosti

P - Projekt vyzkumu a vyvoje financovany z verejnych zdroju (s odkazem do CEP)

Rok uplatnění

2004

Kód důvěrnosti údajů

S - Úplné a pravdivé údaje o projektu nepodléhají ochraně podle zvláštních právních předpisů

Název periodika

Archives of Metallurgy and Materials

ISSN

1733-349

e-ISSN

—

Svazek periodika

49

Číslo periodika v rámci svazku

3

Stát vydavatele periodika

PL - Polská republika

Počet stran výsledku

12

Strana od-do

469-480

Kód UT WoS článku

—

EID výsledku v databázi Scopus

—