Vztah mezi strukturou a vlastnostmi nových hybridních sítí na bázi poly(imid-amid)-poly(ethylen glykol)
Identifikátory výsledku
Kód výsledku v IS VaVaI
<a href="https://www.isvavai.cz/riv?ss=detail&h=RIV%2F00216224%3A14310%2F06%3A00016589" target="_blank" >RIV/00216224:14310/06:00016589 - isvavai.cz</a>
Nalezeny alternativní kódy
RIV/60461373:22310/06:00020153
Výsledek na webu
—
DOI - Digital Object Identifier
—
Alternativní jazyky
Jazyk výsledku
angličtina
Název v původním jazyce
Structure-property relationships in novel poly(imide-amide)-poly(ethylene glycol) hybrid networks
Popis výsledku v původním jazyce
Broadband dielec. relaxation spectroscopy (DRS), thermally stimulated depolarisation currents (TSDC), differential scanning calorimetry (DSC) and to a lesser extent water uptake measurements, were employed to investigate mol. mobility, morphol. and crystn./melting events of PEG in poly(imide-amide)-polyethylene glycol hybrid networks (PIA-PEG) with short (M n=1000 g/mol) and long (M n=3400 g/mol) PEG crosslinks. The results obtained suggest long range connectivity of the PEG component in the hybrids with short PEG crosslinks at PEG content higher than 40 wt% and in these with long PEG crosslinks at PEG content higher than 20 wt%. Crystn. of the PEG component is obsd. by DSC in the hybrids with the longer crosslinks at sufficiently high content of PEG,only. The glass transition temp., T g, of PEG component in the hybrids with the shorter PEG crosslinks is shifted to higher temps. compared to that of the hybrids with longer PEG crosslinks, while suppression of the glass transition of th
Název v anglickém jazyce
Structure-property relationships in novel poly(imide-amide)-poly(ethylene glycol) hybrid networks
Popis výsledku anglicky
Broadband dielec. relaxation spectroscopy (DRS), thermally stimulated depolarisation currents (TSDC), differential scanning calorimetry (DSC) and to a lesser extent water uptake measurements, were employed to investigate mol. mobility, morphol. and crystn./melting events of PEG in poly(imide-amide)-polyethylene glycol hybrid networks (PIA-PEG) with short (M n=1000 g/mol) and long (M n=3400 g/mol) PEG crosslinks. The results obtained suggest long range connectivity of the PEG component in the hybrids with short PEG crosslinks at PEG content higher than 40 wt% and in these with long PEG crosslinks at PEG content higher than 20 wt%. Crystn. of the PEG component is obsd. by DSC in the hybrids with the longer crosslinks at sufficiently high content of PEG,only. The glass transition temp., T g, of PEG component in the hybrids with the shorter PEG crosslinks is shifted to higher temps. compared to that of the hybrids with longer PEG crosslinks, while suppression of the glass transition of th
Klasifikace
Druh
J<sub>x</sub> - Nezařazeno - Článek v odborném periodiku (Jimp, Jsc a Jost)
CEP obor
CD - Makromolekulární chemie
OECD FORD obor
—
Návaznosti výsledku
Projekt
<a href="/cs/project/GA104%2F03%2F0388" target="_blank" >GA104/03/0388: Separace par organických látek ze vzduchu pomocí polymerních membrán</a><br>
Návaznosti
S - Specificky vyzkum na vysokych skolach
Ostatní
Rok uplatnění
2006
Kód důvěrnosti údajů
S - Úplné a pravdivé údaje o projektu nepodléhají ochraně podle zvláštních právních předpisů
Údaje specifické pro druh výsledku
Název periodika
Polymer
ISSN
0032-3861
e-ISSN
—
Svazek periodika
47
Číslo periodika v rámci svazku
1
Stát vydavatele periodika
CZ - Česká republika
Počet stran výsledku
10
Strana od-do
357-366
Kód UT WoS článku
—
EID výsledku v databázi Scopus
—