MICROWAVE PLASMA SYNTHESIS OF IRON NANOPARTICLES

Kód výsledku v IS VaVaI

<a href="https://www.isvavai.cz/riv?ss=detail&h=RIV%2F00216224%3A14310%2F10%3A00040638" target="_blank" >RIV/00216224:14310/10:00040638 - isvavai.cz</a>

Výsledek na webu

—

DOI - Digital Object Identifier

—

Jazyk výsledku

angličtina

Název v původním jazyce

MICROWAVE PLASMA SYNTHESIS OF IRON NANOPARTICLES

Popis výsledku v původním jazyce

Microwave discharges offer wide range of experimental conditions for synthesis of various iron nanoparticles, including iron oxides, carbides and nitrides. In our work two types of discharges were used: i) microwave plasma torch operating at atmosphericpressure and ii) low pressure surface wave discharge. Ultrafine iron nanoparticles (ala-Fe, diameter of 10 nm and less) were produced by plasma decomposition of iron pentacarbonyl (0.1 g to 1 g per hour) in argon or a mixture of iron pentacarbonyl and hydrogen. In case of iron oxides synthesis, oxygen was added to the gas mixture instead of hydrogen. Pure fractions of iron oxides were synthesized. Synthesis of the iron carbides and nitrides was also investigated. In this case hydrocarbon or ammonia wasadded to the gas mixture. The plasma was monitored by optical emission spectroscopy. The samples composition was investigated by XRD,HR-TEM and Mössbauer spectroscopy.

Název v anglickém jazyce

MICROWAVE PLASMA SYNTHESIS OF IRON NANOPARTICLES

Popis výsledku anglicky

Microwave discharges offer wide range of experimental conditions for synthesis of various iron nanoparticles, including iron oxides, carbides and nitrides. In our work two types of discharges were used: i) microwave plasma torch operating at atmosphericpressure and ii) low pressure surface wave discharge. Ultrafine iron nanoparticles (ala-Fe, diameter of 10 nm and less) were produced by plasma decomposition of iron pentacarbonyl (0.1 g to 1 g per hour) in argon or a mixture of iron pentacarbonyl and hydrogen. In case of iron oxides synthesis, oxygen was added to the gas mixture instead of hydrogen. Pure fractions of iron oxides were synthesized. Synthesis of the iron carbides and nitrides was also investigated. In this case hydrocarbon or ammonia wasadded to the gas mixture. The plasma was monitored by optical emission spectroscopy. The samples composition was investigated by XRD,HR-TEM and Mössbauer spectroscopy.

Druh

D - Stať ve sborníku

CEP obor

BL - Fyzika plasmatu a výboje v plynech

OECD FORD obor

—

Projekt

Výsledek vznikl pri realizaci vícero projektů. Více informací v záložce Projekty.

Návaznosti

Z - Vyzkumny zamer (s odkazem do CEZ)<br>S - Specificky vyzkum na vysokych skolach<br>V - Vyzkumna aktivita podporovana z jinych verejnych zdroju

Rok uplatnění

2010

Kód důvěrnosti údajů

S - Úplné a pravdivé údaje o projektu nepodléhají ochraně podle zvláštních právních předpisů

Název statě ve sborníku

Nanocon 2010 Conference Proceedings

ISBN

978-80-87294-18-5

ISSN

—

e-ISSN

—

Počet stran výsledku

100

Strana od-do

—

Název nakladatele

TANGER Ltd.

Místo vydání

Ostrava

Místo konání akce

Olomouc

Datum konání akce

12. 10. 2010

Typ akce podle státní příslušnosti

WRD - Celosvětová akce

Kód UT WoS článku

—