Plasmachemical synthesis of maghemite nanoparticles in atmospheric pressure microwave torch

Kód výsledku v IS VaVaI
<a href="https://www.isvavai.cz/riv?ss=detail&h=RIV%2F00216224%3A14310%2F11%3A00049686" target="_blank" >RIV/00216224:14310/11:00049686 - isvavai.cz</a>
Nalezeny alternativní kódy
RIV/68081723:_____/11:00369514
Výsledek na webu
<a href="http://dx.doi.org/10.1016/j.matlet.2010.12.048" target="_blank" >http://dx.doi.org/10.1016/j.matlet.2010.12.048</a>
DOI - Digital Object Identifier
<a href="http://dx.doi.org/10.1016/j.matlet.2010.12.048" target="_blank" >10.1016/j.matlet.2010.12.048</a>

Jazyk výsledku
angličtina
Název v původním jazyce
Plasmachemical synthesis of maghemite nanoparticles in atmospheric pressure microwave torch
Popis výsledku v původním jazyce
The powder of gama - Fe2O3 nanoparticles was synthesized in microwave torch at atmospheric pressure from 0.05 sccm of Fe(CO)5 vapors in 670 sccm of argon. The optimization of the torch reactor design and deposition conditions allowed continual synthesisof gama - Fe2O3 nanoparticles at low power consumption. The synthesized powder was collected at the reactor walls and analyzed by TEM, X-ray diffraction and Raman spectroscopy without any further purification or treatment. The mean diameter of NPs, as observed by TEM, was 12 nm with a 90% confidence interval 5.5-22 nm.
Název v anglickém jazyce
Plasmachemical synthesis of maghemite nanoparticles in atmospheric pressure microwave torch
Popis výsledku anglicky
The powder of gama - Fe2O3 nanoparticles was synthesized in microwave torch at atmospheric pressure from 0.05 sccm of Fe(CO)5 vapors in 670 sccm of argon. The optimization of the torch reactor design and deposition conditions allowed continual synthesisof gama - Fe2O3 nanoparticles at low power consumption. The synthesized powder was collected at the reactor walls and analyzed by TEM, X-ray diffraction and Raman spectroscopy without any further purification or treatment. The mean diameter of NPs, as observed by TEM, was 12 nm with a 90% confidence interval 5.5-22 nm.

Druh
J<sub>x</sub> - Nezařazeno - Článek v odborném periodiku (Jimp, Jsc a Jost)
CEP obor
BL - Fyzika plasmatu a výboje v plynech
OECD FORD obor
—

Projekt
Výsledek vznikl pri realizaci vícero projektů. Více informací v záložce Projekty.
Návaznosti
P - Projekt vyzkumu a vyvoje financovany z verejnych zdroju (s odkazem do CEP)<br>Z - Vyzkumny zamer (s odkazem do CEZ)

Rok uplatnění
2011
Kód důvěrnosti údajů
S - Úplné a pravdivé údaje o projektu nepodléhají ochraně podle zvláštních právních předpisů

Podobné výsledky(10)