Název v původním jazyce

Synthesis and characterization of AgSn nanoparticles

Popis výsledku v původním jazyce

AgSn nanoparticles were prepared by wet synthesis from silver nitrate and stannous ethylhexanoate by reduction with NaBH4 in temperature range from 0 to -20 degrees of Celsius in methanol under a nitrogen atmosphere.. The resulting product was characterized by SEM, TEM, DSC and XRD methods. DSC method observed melting point depression. The magnitude of this effect depended on the size of obtained nanoparticles.

Název v anglickém jazyce

Synthesis and characterization of AgSn nanoparticles

Popis výsledku anglicky

AgSn nanoparticles were prepared by wet synthesis from silver nitrate and stannous ethylhexanoate by reduction with NaBH4 in temperature range from 0 to -20 degrees of Celsius in methanol under a nitrogen atmosphere.. The resulting product was characterized by SEM, TEM, DSC and XRD methods. DSC method observed melting point depression. The magnitude of this effect depended on the size of obtained nanoparticles.

Druh

O - Ostatní výsledky

CEP obor

CF - Fyzikální chemie a teoretická chemie

OECD FORD obor

—

Projekt

<a href="/cs/project/GA106%2F09%2F0700" target="_blank" >GA106/09/0700: Termodynamika a mikrostruktura nanopráškových pájek šetrných k životnímu prostředí</a><br>

Návaznosti

P - Projekt vyzkumu a vyvoje financovany z verejnych zdroju (s odkazem do CEP)

Rok uplatnění

2011

Kód důvěrnosti údajů

S - Úplné a pravdivé údaje o projektu nepodléhají ochraně podle zvláštních právních předpisů