MECHANICAL STABILITY OF THE P-I-N SOLAR CELLS STUDIED BY INDENTATION METHOD

Kód výsledku v IS VaVaI

<a href="https://www.isvavai.cz/riv?ss=detail&h=RIV%2F00216224%3A14310%2F12%3A00057156" target="_blank" >RIV/00216224:14310/12:00057156 - isvavai.cz</a>

Výsledek na webu

<a href="http://www.chemicke-listy.cz/common/content-issue_s5-volume_106-year_2012.html" target="_blank" >http://www.chemicke-listy.cz/common/content-issue_s5-volume_106-year_2012.html</a>

DOI - Digital Object Identifier

—

Jazyk výsledku

angličtina

Název v původním jazyce

MECHANICAL STABILITY OF THE P-I-N SOLAR CELLS STUDIED BY INDENTATION METHOD

Popis výsledku v původním jazyce

The main priorities when preparing the p-i-n amorphous silicon based solar cells are the efficiency as well as the optoelectronic stability of the cells. However, for the final applications, a good mechanical and thermomechanical stability is not of thesecond order of importance. The large internal mechanical stress, weak adhesion can result the deterioration of the solar cell (cracking, delamination). The objective of our study was to investigate the mechanical properties of p-i-n amorphous silicon based solar cells by means of depth sensing indentation technique (Fisherscope H100). The instrumented indentation method combined with the study of the morphology of the indentation prints enable us to determinate microhardness, fracture toughness of theinterface with substrate and internal stress.

Název v anglickém jazyce

MECHANICAL STABILITY OF THE P-I-N SOLAR CELLS STUDIED BY INDENTATION METHOD

Popis výsledku anglicky

The main priorities when preparing the p-i-n amorphous silicon based solar cells are the efficiency as well as the optoelectronic stability of the cells. However, for the final applications, a good mechanical and thermomechanical stability is not of thesecond order of importance. The large internal mechanical stress, weak adhesion can result the deterioration of the solar cell (cracking, delamination). The objective of our study was to investigate the mechanical properties of p-i-n amorphous silicon based solar cells by means of depth sensing indentation technique (Fisherscope H100). The instrumented indentation method combined with the study of the morphology of the indentation prints enable us to determinate microhardness, fracture toughness of theinterface with substrate and internal stress.

Druh

J_x - Nezařazeno - Článek v odborném periodiku (Jimp, Jsc a Jost)

CEP obor

BL - Fyzika plasmatu a výboje v plynech

OECD FORD obor

—

Projekt

Výsledek vznikl pri realizaci vícero projektů. Více informací v záložce Projekty.

Návaznosti

P - Projekt vyzkumu a vyvoje financovany z verejnych zdroju (s odkazem do CEP)

Rok uplatnění

2012

Kód důvěrnosti údajů

S - Úplné a pravdivé údaje o projektu nepodléhají ochraně podle zvláštních právních předpisů

Název periodika

Chemické listy

ISSN

0009-2770

e-ISSN

—

Svazek periodika

106/2012

Číslo periodika v rámci svazku

S5

Stát vydavatele periodika

CZ - Česká republika

Počet stran výsledku

4

Strana od-do

1491-1494

Kód UT WoS článku

—

EID výsledku v databázi Scopus

—