Air DCSBD plasma treatment of Al surface at atmospheric pressure

Kód výsledku v IS VaVaI

<a href="https://www.isvavai.cz/riv?ss=detail&h=RIV%2F00216224%3A14310%2F12%3A00057287" target="_blank" >RIV/00216224:14310/12:00057287 - isvavai.cz</a>

Výsledek na webu

<a href="http://www.sciencedirect.com/science/article/pii/S0257897211012588" target="_blank" >http://www.sciencedirect.com/science/article/pii/S0257897211012588</a>

DOI - Digital Object Identifier

<a href="http://dx.doi.org/10.1016/j.surfcoat.2011.12.039" target="_blank" >10.1016/j.surfcoat.2011.12.039</a>

Jazyk výsledku

angličtina

Název v původním jazyce

Air DCSBD plasma treatment of Al surface at atmospheric pressure

Popis výsledku v původním jazyce

The ambient air plasma cleaning and activation effects on aluminum surface using the Diffuse Coplanar Surface Barrier Discharge in ambient air are presented. Atomic Force Microscopy, Attenuated Total Reflectance FTIR and Laser Desorption/Ionization Time-of-Flight Mass Spectroscopy techniques were used to characterize the changes on the surface before and after plasma treatments. The plasma cleaning effect on aluminum, i.e. decrease of hydrocarbon contamination, was proven. Also the air plasma treatmentresulted in a significant increase of amount of OH groups on the surface and in a decrease of the surface roughness.

Název v anglickém jazyce

Air DCSBD plasma treatment of Al surface at atmospheric pressure

Popis výsledku anglicky

The ambient air plasma cleaning and activation effects on aluminum surface using the Diffuse Coplanar Surface Barrier Discharge in ambient air are presented. Atomic Force Microscopy, Attenuated Total Reflectance FTIR and Laser Desorption/Ionization Time-of-Flight Mass Spectroscopy techniques were used to characterize the changes on the surface before and after plasma treatments. The plasma cleaning effect on aluminum, i.e. decrease of hydrocarbon contamination, was proven. Also the air plasma treatmentresulted in a significant increase of amount of OH groups on the surface and in a decrease of the surface roughness.

Druh

J_x - Nezařazeno - Článek v odborném periodiku (Jimp, Jsc a Jost)

CEP obor

BL - Fyzika plasmatu a výboje v plynech

OECD FORD obor

—

Projekt

<a href="/cs/project/GA202%2F07%2F1669" target="_blank" >GA202/07/1669: Depozice termomechanicky stabilních nanostrukturovaných diamantu-podobných tenkých vrstev ve dvojfrekvenčních kapacitních výbojích</a><br>

Návaznosti

P - Projekt vyzkumu a vyvoje financovany z verejnych zdroju (s odkazem do CEP)<br>S - Specificky vyzkum na vysokych skolach

Rok uplatnění

2012

Kód důvěrnosti údajů

S - Úplné a pravdivé údaje o projektu nepodléhají ochraně podle zvláštních právních předpisů

Název periodika

Surface and Coatings Technology

ISSN

0257-8972

e-ISSN

—

Svazek periodika

206

Číslo periodika v rámci svazku

11-12

Stát vydavatele periodika

CH - Švýcarská konfederace

Počet stran výsledku

6

Strana od-do

3011-3016

Kód UT WoS článku

000301017300040

EID výsledku v databázi Scopus

—