Study of the thermal dependence of mechanical properties, chemical composition and structure of nanocomposite TiC/a-C:H coatings
Identifikátory výsledku
Kód výsledku v IS VaVaI
<a href="https://www.isvavai.cz/riv?ss=detail&h=RIV%2F00216224%3A14310%2F14%3A00073525" target="_blank" >RIV/00216224:14310/14:00073525 - isvavai.cz</a>
Nalezeny alternativní kódy
RIV/68081723:_____/14:00428393 RIV/61389005:_____/14:00428393
Výsledek na webu
<a href="http://dx.doi.org/10.1016/j.surfcoat.2014.01.019" target="_blank" >http://dx.doi.org/10.1016/j.surfcoat.2014.01.019</a>
DOI - Digital Object Identifier
<a href="http://dx.doi.org/10.1016/j.surfcoat.2014.01.019" target="_blank" >10.1016/j.surfcoat.2014.01.019</a>
Alternativní jazyky
Jazyk výsledku
angličtina
Název v původním jazyce
Study of the thermal dependence of mechanical properties, chemical composition and structure of nanocomposite TiC/a-C:H coatings
Popis výsledku v původním jazyce
This work is aimed at the study of thermal stability of nc-TiC/a-C:H coatings deposited on steel substrates by unbalanced reactivemagnetron sputtering of titanium in an acetylene containing atmosphere. The as-deposited coatings show high hardness and elastic modulus together with low wear and low friction coefficients. The coating properties were investigated as a function of annealing temperature using thermal desorption spectroscopy under UHV conditions. The hardness and elastic modulus did not changesubstantially up to 700 deg.C compared to the properties of the as-deposited coatings. Themost significant changeswere observed in case of their fracture toughness,which decreased due to the hydrogen loss from amorphous carbon matrix.
Název v anglickém jazyce
Study of the thermal dependence of mechanical properties, chemical composition and structure of nanocomposite TiC/a-C:H coatings
Popis výsledku anglicky
This work is aimed at the study of thermal stability of nc-TiC/a-C:H coatings deposited on steel substrates by unbalanced reactivemagnetron sputtering of titanium in an acetylene containing atmosphere. The as-deposited coatings show high hardness and elastic modulus together with low wear and low friction coefficients. The coating properties were investigated as a function of annealing temperature using thermal desorption spectroscopy under UHV conditions. The hardness and elastic modulus did not changesubstantially up to 700 deg.C compared to the properties of the as-deposited coatings. Themost significant changeswere observed in case of their fracture toughness,which decreased due to the hydrogen loss from amorphous carbon matrix.
Klasifikace
Druh
J<sub>x</sub> - Nezařazeno - Článek v odborném periodiku (Jimp, Jsc a Jost)
CEP obor
BL - Fyzika plasmatu a výboje v plynech
OECD FORD obor
—
Návaznosti výsledku
Projekt
Výsledek vznikl pri realizaci vícero projektů. Více informací v záložce Projekty.
Návaznosti
P - Projekt vyzkumu a vyvoje financovany z verejnych zdroju (s odkazem do CEP)
Ostatní
Rok uplatnění
2014
Kód důvěrnosti údajů
S - Úplné a pravdivé údaje o projektu nepodléhají ochraně podle zvláštních právních předpisů
Údaje specifické pro druh výsledku
Název periodika
Surface & coatings technology
ISSN
0257-8972
e-ISSN
—
Svazek periodika
242
Číslo periodika v rámci svazku
March
Stát vydavatele periodika
CH - Švýcarská konfederace
Počet stran výsledku
6
Strana od-do
62-67
Kód UT WoS článku
000333782400009
EID výsledku v databázi Scopus
—