Temperature Stability of AgCu Nanoparticles
Identifikátory výsledku
Kód výsledku v IS VaVaI
<a href="https://www.isvavai.cz/riv?ss=detail&h=RIV%2F00216224%3A14310%2F15%3A00081656" target="_blank" >RIV/00216224:14310/15:00081656 - isvavai.cz</a>
Nalezeny alternativní kódy
RIV/68081723:_____/15:00462329
Výsledek na webu
<a href="http://dx.doi.org/10.1007/s11051-015-3288-7" target="_blank" >http://dx.doi.org/10.1007/s11051-015-3288-7</a>
DOI - Digital Object Identifier
<a href="http://dx.doi.org/10.1007/s11051-015-3288-7" target="_blank" >10.1007/s11051-015-3288-7</a>
Alternativní jazyky
Jazyk výsledku
angličtina
Název v původním jazyce
Temperature Stability of AgCu Nanoparticles
Popis výsledku v původním jazyce
The colloidal solutions of the Ag-Cu nanoparticles (NPs, 10-32 nm) were prepared by solvothermal reactions. The samples of dried AgCu NPs and the resulting microstructures after heat treatment in air were investigated by various methods including electron microscopy (TEM, SEM) and high-temperature X-ray powder diffraction (HTXRD). The AgCu randomly mixed, Cu-rich, and Ag-rich face centred cubic crystal lattices were detected during the experiments. The temperature induced sintering was observed experimentally by HTXRD at 250 degrees C. The phase transformations at high temperatures were monitored by differential scanning calorimetry. The formation of the Ag-rich grains during heating in air and evolution of copper oxide microstructure were detected.
Název v anglickém jazyce
Temperature Stability of AgCu Nanoparticles
Popis výsledku anglicky
The colloidal solutions of the Ag-Cu nanoparticles (NPs, 10-32 nm) were prepared by solvothermal reactions. The samples of dried AgCu NPs and the resulting microstructures after heat treatment in air were investigated by various methods including electron microscopy (TEM, SEM) and high-temperature X-ray powder diffraction (HTXRD). The AgCu randomly mixed, Cu-rich, and Ag-rich face centred cubic crystal lattices were detected during the experiments. The temperature induced sintering was observed experimentally by HTXRD at 250 degrees C. The phase transformations at high temperatures were monitored by differential scanning calorimetry. The formation of the Ag-rich grains during heating in air and evolution of copper oxide microstructure were detected.
Klasifikace
Druh
J<sub>x</sub> - Nezařazeno - Článek v odborném periodiku (Jimp, Jsc a Jost)
CEP obor
JJ - Ostatní materiály
OECD FORD obor
—
Návaznosti výsledku
Projekt
Výsledek vznikl pri realizaci vícero projektů. Více informací v záložce Projekty.
Návaznosti
P - Projekt vyzkumu a vyvoje financovany z verejnych zdroju (s odkazem do CEP)
Ostatní
Rok uplatnění
2015
Kód důvěrnosti údajů
S - Úplné a pravdivé údaje o projektu nepodléhají ochraně podle zvláštních právních předpisů
Údaje specifické pro druh výsledku
Název periodika
Journal of Nanoparticle Ressearch
ISSN
1388-0764
e-ISSN
—
Svazek periodika
17
Číslo periodika v rámci svazku
12
Stát vydavatele periodika
NL - Nizozemsko
Počet stran výsledku
7
Strana od-do
"nestránkováno"
Kód UT WoS článku
000368506700001
EID výsledku v databázi Scopus
—