Low-Temperature hydrogenation of diamond nanoparticles using diffuse coplanar surface barrier discharge at atmospheric pressure

Kód výsledku v IS VaVaI

<a href="https://www.isvavai.cz/riv?ss=detail&h=RIV%2F00216224%3A14310%2F15%3A00083402" target="_blank" >RIV/00216224:14310/15:00083402 - isvavai.cz</a>

Nalezeny alternativní kódy

RIV/68378271:_____/15:00454760

Výsledek na webu

<a href="http://dx.doi.org/10.1002/pssb.201552232" target="_blank" >http://dx.doi.org/10.1002/pssb.201552232</a>

DOI - Digital Object Identifier

<a href="http://dx.doi.org/10.1002/pssb.201552232" target="_blank" >10.1002/pssb.201552232</a>

Jazyk výsledku

angličtina

Název v původním jazyce

Low-Temperature hydrogenation of diamond nanoparticles using diffuse coplanar surface barrier discharge at atmospheric pressure

Popis výsledku v původním jazyce

Due to an extraordinary combination of intrinsic properties of diamond nanoparticles (DNPs), there is an increased demand for their usage in various areas. While a broad range of surface termination is often done by wet-chemical, UV-irradiation or plasmatreatments, DNPs hydrogenation is still an open issue. Thermal annealing or microwave plasma treatment, both known as high-temperature processes, do not offer satisfactory solutions for DNPs hydrogenation. Here, we report on a new approach for plasma-assisted DNPs hydrogenation at temperatures below 100 °C. As-received detonation DNPs with size about 5 nm were annealed (oxidized) in air at 450 °C for 30 min to reduce non-diamond carbon content. Then the annealed DNPs were plasma treated using atmospheric-pressure diffuse coplanar surface barrier discharge in pure hydrogen at powers densities of 1.8 and 3.1 W/cm2.

Název v anglickém jazyce

Low-Temperature hydrogenation of diamond nanoparticles using diffuse coplanar surface barrier discharge at atmospheric pressure

Popis výsledku anglicky

Due to an extraordinary combination of intrinsic properties of diamond nanoparticles (DNPs), there is an increased demand for their usage in various areas. While a broad range of surface termination is often done by wet-chemical, UV-irradiation or plasmatreatments, DNPs hydrogenation is still an open issue. Thermal annealing or microwave plasma treatment, both known as high-temperature processes, do not offer satisfactory solutions for DNPs hydrogenation. Here, we report on a new approach for plasma-assisted DNPs hydrogenation at temperatures below 100 °C. As-received detonation DNPs with size about 5 nm were annealed (oxidized) in air at 450 °C for 30 min to reduce non-diamond carbon content. Then the annealed DNPs were plasma treated using atmospheric-pressure diffuse coplanar surface barrier discharge in pure hydrogen at powers densities of 1.8 and 3.1 W/cm2.

Druh

J_x - Nezařazeno - Článek v odborném periodiku (Jimp, Jsc a Jost)

CEP obor

BL - Fyzika plasmatu a výboje v plynech

OECD FORD obor

—

Projekt

Výsledek vznikl pri realizaci vícero projektů. Více informací v záložce Projekty.

Návaznosti

P - Projekt vyzkumu a vyvoje financovany z verejnych zdroju (s odkazem do CEP)

Rok uplatnění

2015

Kód důvěrnosti údajů

S - Úplné a pravdivé údaje o projektu nepodléhají ochraně podle zvláštních právních předpisů

Název periodika

physica status solidi (b)

ISSN

0370-1972

e-ISSN

—

Svazek periodika

252

Číslo periodika v rámci svazku

11

Stát vydavatele periodika

DE - Spolková republika Německo

Počet stran výsledku

6

Strana od-do

2602-2607

Kód UT WoS článku

000364690400042

EID výsledku v databázi Scopus

—