Atmospheric pressure plasma treatment of polyamide-12 foils
Identifikátory výsledku
Kód výsledku v IS VaVaI
<a href="https://www.isvavai.cz/riv?ss=detail&h=RIV%2F00216224%3A14310%2F15%3A00114954" target="_blank" >RIV/00216224:14310/15:00114954 - isvavai.cz</a>
Výsledek na webu
<a href="http://www.degruyter.com/view/j/chem.2015.13.issue-1/chem-2015-0049/chem-2015-0049.xml" target="_blank" >http://www.degruyter.com/view/j/chem.2015.13.issue-1/chem-2015-0049/chem-2015-0049.xml</a>
DOI - Digital Object Identifier
<a href="http://dx.doi.org/10.1515/chem-2015-0049" target="_blank" >10.1515/chem-2015-0049</a>
Alternativní jazyky
Jazyk výsledku
angličtina
Název v původním jazyce
Atmospheric pressure plasma treatment of polyamide-12 foils
Popis výsledku v původním jazyce
The surface of a polyamide-12 (PA-12) foil was modified in order to improve the adhesive properties by two types of atmospheric pressure plasma sources. The samples were characterized using contact angle measurement, adhesive properties measurement and X-ray photoelectron spectroscopy (XPS). The ageing of the plasma modification was also studied. A significant increase in wettability was observed at different treatment times. The same effect was also seen in the adhesive properties - the adhesion was increased almost 12 times for 10 s DCSBD treatment in comparison to untreated PA-12. XPS analysis confirmed chemical changes due to the plasma modification of the PA-12. It was concluded that both plasma sources improve the adhesive properties of PA-12, with DCSBD obtaining better results.
Název v anglickém jazyce
Atmospheric pressure plasma treatment of polyamide-12 foils
Popis výsledku anglicky
The surface of a polyamide-12 (PA-12) foil was modified in order to improve the adhesive properties by two types of atmospheric pressure plasma sources. The samples were characterized using contact angle measurement, adhesive properties measurement and X-ray photoelectron spectroscopy (XPS). The ageing of the plasma modification was also studied. A significant increase in wettability was observed at different treatment times. The same effect was also seen in the adhesive properties - the adhesion was increased almost 12 times for 10 s DCSBD treatment in comparison to untreated PA-12. XPS analysis confirmed chemical changes due to the plasma modification of the PA-12. It was concluded that both plasma sources improve the adhesive properties of PA-12, with DCSBD obtaining better results.
Klasifikace
Druh
J<sub>imp</sub> - Článek v periodiku v databázi Web of Science
CEP obor
—
OECD FORD obor
10305 - Fluids and plasma physics (including surface physics)
Návaznosti výsledku
Projekt
Výsledek vznikl pri realizaci vícero projektů. Více informací v záložce Projekty.
Návaznosti
P - Projekt vyzkumu a vyvoje financovany z verejnych zdroju (s odkazem do CEP)
Ostatní
Rok uplatnění
2015
Kód důvěrnosti údajů
S - Úplné a pravdivé údaje o projektu nepodléhají ochraně podle zvláštních právních předpisů
Údaje specifické pro druh výsledku
Název periodika
Open Chemistry
ISSN
2391-5420
e-ISSN
—
Svazek periodika
13
Číslo periodika v rámci svazku
1
Stát vydavatele periodika
PL - Polská republika
Počet stran výsledku
7
Strana od-do
382-388
Kód UT WoS článku
000355403100046
EID výsledku v databázi Scopus
2-s2.0-84982671628