Multigram preparation of tungsten microfibers via needle-less electrospinning of phosphotungstic acid
Identifikátory výsledku
Kód výsledku v IS VaVaI
<a href="https://www.isvavai.cz/riv?ss=detail&h=RIV%2F00216224%3A14310%2F23%3A00130332" target="_blank" >RIV/00216224:14310/23:00130332 - isvavai.cz</a>
Výsledek na webu
<a href="https://doi.org/10.1016/j.ijrmhm.2023.106121" target="_blank" >https://doi.org/10.1016/j.ijrmhm.2023.106121</a>
DOI - Digital Object Identifier
<a href="http://dx.doi.org/10.1016/j.ijrmhm.2023.106121" target="_blank" >10.1016/j.ijrmhm.2023.106121</a>
Alternativní jazyky
Jazyk výsledku
angličtina
Název v původním jazyce
Multigram preparation of tungsten microfibers via needle-less electrospinning of phosphotungstic acid
Popis výsledku v původním jazyce
Metallic tungsten microfibers were prepared in a multigram yield by electrospinning from the aqueous phosphotungstic acid/polyvinyl alcohol (PVA) solution in three steps. Green composite microfibers of H3PW12O40 /PVA were easily electrospun from precursor solutions on a Nanospider instrument with a cylindrical rotating electrode. Subsequent oxidation of the organic PVA matrix and decomposition of phosphotungstic acid in the air at 600°C provided ceramic WO3/P2O5 fibers. Finally, prepared oxide fibers were reduced in a forming gas atmosphere at temperatures up to 1000°C. During the reduction, all phosphorus was removed, and pure metallic tungsten microfibers were produced.
Název v anglickém jazyce
Multigram preparation of tungsten microfibers via needle-less electrospinning of phosphotungstic acid
Popis výsledku anglicky
Metallic tungsten microfibers were prepared in a multigram yield by electrospinning from the aqueous phosphotungstic acid/polyvinyl alcohol (PVA) solution in three steps. Green composite microfibers of H3PW12O40 /PVA were easily electrospun from precursor solutions on a Nanospider instrument with a cylindrical rotating electrode. Subsequent oxidation of the organic PVA matrix and decomposition of phosphotungstic acid in the air at 600°C provided ceramic WO3/P2O5 fibers. Finally, prepared oxide fibers were reduced in a forming gas atmosphere at temperatures up to 1000°C. During the reduction, all phosphorus was removed, and pure metallic tungsten microfibers were produced.
Klasifikace
Druh
J<sub>imp</sub> - Článek v periodiku v databázi Web of Science
CEP obor
—
OECD FORD obor
10400 - Chemical sciences
Návaznosti výsledku
Projekt
—
Návaznosti
S - Specificky vyzkum na vysokych skolach<br>I - Institucionalni podpora na dlouhodoby koncepcni rozvoj vyzkumne organizace
Ostatní
Rok uplatnění
2023
Kód důvěrnosti údajů
S - Úplné a pravdivé údaje o projektu nepodléhají ochraně podle zvláštních právních předpisů
Údaje specifické pro druh výsledku
Název periodika
International Journal of Refractory Metals and Hard Materials
ISSN
0263-4368
e-ISSN
0263-4368
Svazek periodika
112
Číslo periodika v rámci svazku
April
Stát vydavatele periodika
GB - Spojené království Velké Británie a Severního Irska
Počet stran výsledku
9
Strana od-do
1-9
Kód UT WoS článku
000926868100001
EID výsledku v databázi Scopus
2-s2.0-85146829105