Adhesion improvement on the inner side of LLDPE/PA tubular film exposed to DCSBD roll-to-roll plasma system from the outer side of the film

Kód výsledku v IS VaVaI

<a href="https://www.isvavai.cz/riv?ss=detail&h=RIV%2F00216224%3A14310%2F23%3A00130339" target="_blank" >RIV/00216224:14310/23:00130339 - isvavai.cz</a>

Výsledek na webu

<a href="https://doi.org/10.1002/ppap.202200226" target="_blank" >https://doi.org/10.1002/ppap.202200226</a>

DOI - Digital Object Identifier

<a href="http://dx.doi.org/10.1002/ppap.202200226" target="_blank" >10.1002/ppap.202200226</a>

Jazyk výsledku

angličtina

Název v původním jazyce

Adhesion improvement on the inner side of LLDPE/PA tubular film exposed to DCSBD roll-to-roll plasma system from the outer side of the film

Popis výsledku v původním jazyce

Diffuse coplanar surface barrier discharge (DCSBD) was used to activate the opposite side of the plasma-exposed linear low-density polyethylene/polyamide (LLDPE/PA) tubular film of multilayer casing. We determined that conductive metal rubber roller in the DCSBD system allowed the formation of microfilaments perpendicular to the film surface, resulting in improved wettability and adhesion of inner LLDPE side of the tubular film. These findings were supported by increasing the concentration of polar functional groups. Based on these remarkable outcomes obtained after a very short plasma exposure time of 0.5 s, DCSBD roll-to-roll system in proper arrangement affords adhesion improvement of the opposite side of the treated film without any material damage, hence can compete with industrial corona in commercial sphere of plasma treatments.

Název v anglickém jazyce

Adhesion improvement on the inner side of LLDPE/PA tubular film exposed to DCSBD roll-to-roll plasma system from the outer side of the film

Popis výsledku anglicky

Diffuse coplanar surface barrier discharge (DCSBD) was used to activate the opposite side of the plasma-exposed linear low-density polyethylene/polyamide (LLDPE/PA) tubular film of multilayer casing. We determined that conductive metal rubber roller in the DCSBD system allowed the formation of microfilaments perpendicular to the film surface, resulting in improved wettability and adhesion of inner LLDPE side of the tubular film. These findings were supported by increasing the concentration of polar functional groups. Based on these remarkable outcomes obtained after a very short plasma exposure time of 0.5 s, DCSBD roll-to-roll system in proper arrangement affords adhesion improvement of the opposite side of the treated film without any material damage, hence can compete with industrial corona in commercial sphere of plasma treatments.

Druh

J_imp - Článek v periodiku v databázi Web of Science

CEP obor

—

OECD FORD obor

10305 - Fluids and plasma physics (including surface physics)

Projekt

<a href="/cs/project/LM2018097" target="_blank" >LM2018097: Centrum výzkumu a vývoje plazmatu a nanotechnologických povrchových úprav</a><br>

Návaznosti

P - Projekt vyzkumu a vyvoje financovany z verejnych zdroju (s odkazem do CEP)<br>I - Institucionalni podpora na dlouhodoby koncepcni rozvoj vyzkumne organizace

Rok uplatnění

2023

Kód důvěrnosti údajů

S - Úplné a pravdivé údaje o projektu nepodléhají ochraně podle zvláštních právních předpisů

Název periodika

Plasma Processes and Polymers

ISSN

1612-8850

e-ISSN

1612-8869

Svazek periodika

20

Číslo periodika v rámci svazku

5

Stát vydavatele periodika

DE - Spolková republika Německo

Počet stran výsledku

13

Strana od-do

1-13

Kód UT WoS článku

000930185800001

EID výsledku v databázi Scopus

2-s2.0-85147919582