The effect of hydroxyapatite particle size on viscoelastic properties and calcium release from a thermosensitive triblock copolymer

Kód výsledku v IS VaVaI

<a href="https://www.isvavai.cz/riv?ss=detail&h=RIV%2F00216224%3A14740%2F17%3A00100465" target="_blank" >RIV/00216224:14740/17:00100465 - isvavai.cz</a>

Nalezeny alternativní kódy

RIV/00216305:26620/17:PU121273

Výsledek na webu

<a href="https://link.springer.com/article/10.1007%2Fs00396-016-3983-7" target="_blank" >https://link.springer.com/article/10.1007%2Fs00396-016-3983-7</a>

DOI - Digital Object Identifier

<a href="http://dx.doi.org/10.1007/s00396-016-3983-7" target="_blank" >10.1007/s00396-016-3983-7</a>

Jazyk výsledku

angličtina

Název v původním jazyce

The effect of hydroxyapatite particle size on viscoelastic properties and calcium release from a thermosensitive triblock copolymer

Popis výsledku v původním jazyce

Well-defined "smart" injectable hydrogel based on hydrophilic poly(ethylene glycol) (PEG) and hydrophobic poly(lactic acid-co-glycolic acid) (PLA/PGA) copolymer (PLGA-PEG-PLGA) gelling at the body temperature was modified by bioactive hydroxyapatite (HAp) in the form of micro-, nano-, and core-shell particles (mu-HAp, n-HAp, and CS-x, respectively) to be applicable as calcium delivery system in bone regeneration. Viscoelastic moduli increased with HAp content as expected. Whereas systems containing mu-HAp or CS-x particles maintained two sol-gel and gel-sol phase transitions, the n-HAp containing system showed only one sol-gel phase transition due to the strong interactions between polymer chain and the n-HAp surface. In vitro, studies proved the controlled uniform release of calcium cations from both CS-x and n-HAp over the 9-day period without any initial burst release.

Název v anglickém jazyce

The effect of hydroxyapatite particle size on viscoelastic properties and calcium release from a thermosensitive triblock copolymer

Popis výsledku anglicky

Well-defined "smart" injectable hydrogel based on hydrophilic poly(ethylene glycol) (PEG) and hydrophobic poly(lactic acid-co-glycolic acid) (PLA/PGA) copolymer (PLGA-PEG-PLGA) gelling at the body temperature was modified by bioactive hydroxyapatite (HAp) in the form of micro-, nano-, and core-shell particles (mu-HAp, n-HAp, and CS-x, respectively) to be applicable as calcium delivery system in bone regeneration. Viscoelastic moduli increased with HAp content as expected. Whereas systems containing mu-HAp or CS-x particles maintained two sol-gel and gel-sol phase transitions, the n-HAp containing system showed only one sol-gel phase transition due to the strong interactions between polymer chain and the n-HAp surface. In vitro, studies proved the controlled uniform release of calcium cations from both CS-x and n-HAp over the 9-day period without any initial burst release.

Druh

J_imp - Článek v periodiku v databázi Web of Science

CEP obor

—

OECD FORD obor

10403 - Physical chemistry

Projekt

Výsledek vznikl pri realizaci vícero projektů. Více informací v záložce Projekty.

Návaznosti

P - Projekt vyzkumu a vyvoje financovany z verejnych zdroju (s odkazem do CEP)

Rok uplatnění

2017

Kód důvěrnosti údajů

S - Úplné a pravdivé údaje o projektu nepodléhají ochraně podle zvláštních právních předpisů

Název periodika

COLLOID AND POLYMER SCIENCE

ISSN

0303-402X

e-ISSN

—

Svazek periodika

295

Číslo periodika v rámci svazku

1

Stát vydavatele periodika

US - Spojené státy americké

Počet stran výsledku

9

Strana od-do

107-115

Kód UT WoS článku

000392135800011

EID výsledku v databázi Scopus

2-s2.0-84997284789