Krystalizace CaTi4(PO4)6 z vápenato-titaničitých borofosfátových skel

Kód výsledku v IS VaVaI

<a href="https://www.isvavai.cz/riv?ss=detail&h=RIV%2F00216275%3A25310%2F05%3A00002953" target="_blank" >RIV/00216275:25310/05:00002953 - isvavai.cz</a>

Výsledek na webu

—

DOI - Digital Object Identifier

—

Jazyk výsledku

angličtina

Název v původním jazyce

Crystallization of CaTi4(PO4)6 from calcium-titanium borophosphate glasses

Popis výsledku v původním jazyce

Preparation of the CaTi4(PO4)6-type glass-ceramic materials by controlled crystallization of calcium-titanium borophosphate glasses was studied in the compositional series of 50CaO-10B2O3-40P2O5+xTiO2 (x=0-56 mol% TiO2) and 30CaO-30B2O3-40P2O5+xTiO2 (x=0-24mol% TiO2). The glasses crystallize under heating within the temperature region of 700-800°C and the surface nucleation mechanism prevails in all the TiO2-doped glasses over the internal one. The major compounds formed by crystallization were CaTi4(PO4)6, Ca2P2O7 and BPO4. Changes in the XRD patterns after leaching with 1M HCl or 1M HNO3 showed that the acids dissolve most of all the other crystalline phases than CaTi4(PO4)6. In this way a porous skeleton with CaTi4(PO4)6 phase is formed the specificsurface area of which decreases with increasing TiO2 content in the starting glasses.

Název v anglickém jazyce

Crystallization of CaTi4(PO4)6 from calcium-titanium borophosphate glasses

Popis výsledku anglicky

Preparation of the CaTi4(PO4)6-type glass-ceramic materials by controlled crystallization of calcium-titanium borophosphate glasses was studied in the compositional series of 50CaO-10B2O3-40P2O5+xTiO2 (x=0-56 mol% TiO2) and 30CaO-30B2O3-40P2O5+xTiO2 (x=0-24mol% TiO2). The glasses crystallize under heating within the temperature region of 700-800°C and the surface nucleation mechanism prevails in all the TiO2-doped glasses over the internal one. The major compounds formed by crystallization were CaTi4(PO4)6, Ca2P2O7 and BPO4. Changes in the XRD patterns after leaching with 1M HCl or 1M HNO3 showed that the acids dissolve most of all the other crystalline phases than CaTi4(PO4)6. In this way a porous skeleton with CaTi4(PO4)6 phase is formed the specificsurface area of which decreases with increasing TiO2 content in the starting glasses.

Druh

J_x - Nezařazeno - Článek v odborném periodiku (Jimp, Jsc a Jost)

CEP obor

JH - Keramika, žáruvzdorné materiály a skla

OECD FORD obor

—

Projekt

<a href="/cs/project/GA104%2F04%2F0711" target="_blank" >GA104/04/0711: Borofosfátová a fosfátová skla a sklokeramické materiály se specifickými termomechanickými vlastnostmi</a><br>

Návaznosti

Z - Vyzkumny zamer (s odkazem do CEZ)

Rok uplatnění

2005

Kód důvěrnosti údajů

S - Úplné a pravdivé údaje o projektu nepodléhají ochraně podle zvláštních právních předpisů

Název periodika

Phosphorous Research Bulletin

ISSN

0918-4783

e-ISSN

—

Svazek periodika

—

Číslo periodika v rámci svazku

19

Stát vydavatele periodika

JP - Japonsko

Počet stran výsledku

6

Strana od-do

178-183

Kód UT WoS článku

—

EID výsledku v databázi Scopus

—