Medium range order in lead borophosphate glasses

Popis výsledku v původním jazyce

The structure of 50PbO-xB2O3(50-x)P2O5 glasses with x = 0-25 mol% B2O3 was refined by Raman and 11B MQMAS NMR investigations. The analysis of Raman spectra, using the concentration step of 2 mol% B2O3 within the range of 0-12 mol% B2O3, showed that the evolution of changes in the type of oxygen bridges can be observed from the Raman bands within the range of 600-800 cm-1. 11B MQMAS NMR spectra of glasses with x = 15, 20 and 25 mol% B2O3 revealed the presence of two BO4 sites in these glasses. The firstsite B1O4, characterized by the chemical shift of d = -3.8 - (-3.4) ppm, was assigned to tetrahedral B(OP)4 structural units. Within the concentration range x = 15-25 mol% B2O3 the site B1O4 is gradually replaced by the site B2O4 with the chemical shiftof d = -1.8 - (-1.1) ppm. This second site we assigned to the presence of B(OP)3(OB) units in which the central boron atom is linked to three PO4 groups and one BO3 group.

Název v anglickém jazyce

Medium range order in lead borophosphate glasses

Popis výsledku anglicky

The structure of 50PbO-xB2O3(50-x)P2O5 glasses with x = 0-25 mol% B2O3 was refined by Raman and 11B MQMAS NMR investigations. The analysis of Raman spectra, using the concentration step of 2 mol% B2O3 within the range of 0-12 mol% B2O3, showed that the evolution of changes in the type of oxygen bridges can be observed from the Raman bands within the range of 600-800 cm-1. 11B MQMAS NMR spectra of glasses with x = 15, 20 and 25 mol% B2O3 revealed the presence of two BO4 sites in these glasses. The firstsite B1O4, characterized by the chemical shift of d = -3.8 - (-3.4) ppm, was assigned to tetrahedral B(OP)4 structural units. Within the concentration range x = 15-25 mol% B2O3 the site B1O4 is gradually replaced by the site B2O4 with the chemical shiftof d = -1.8 - (-1.1) ppm. This second site we assigned to the presence of B(OP)3(OB) units in which the central boron atom is linked to three PO4 groups and one BO3 group.

Druh

J_x - Nezařazeno - Článek v odborném periodiku (Jimp, Jsc a Jost)

CEP obor

JH - Keramika, žáruvzdorné materiály a skla

OECD FORD obor

—

Projekt

<a href="/cs/project/GA104%2F04%2F0711" target="_blank" >GA104/04/0711: Borofosfátová a fosfátová skla a sklokeramické materiály se specifickými termomechanickými vlastnostmi</a><br>

Návaznosti

Z - Vyzkumny zamer (s odkazem do CEZ)

Rok uplatnění

2006

Kód důvěrnosti údajů

S - Úplné a pravdivé údaje o projektu nepodléhají ochraně podle zvláštních právních předpisů

Název periodika

Physics and Chemistry of Glasses: European Journal of Glass Science and Technology B

ISSN

0031-9090

e-ISSN

—

Svazek periodika

—

Číslo periodika v rámci svazku

47

Stát vydavatele periodika

GB - Spojené království Velké Británie a Severního Irska

Počet stran výsledku

6

Strana od-do

471-475

Kód UT WoS článku

—

EID výsledku v databázi Scopus

—