Struktura a vlastnosti borofosfátových skel s obsahem Sb2O3

Kód výsledku v IS VaVaI

<a href="https://www.isvavai.cz/riv?ss=detail&h=RIV%2F00216275%3A25310%2F07%3A00005827" target="_blank" >RIV/00216275:25310/07:00005827 - isvavai.cz</a>

Výsledek na webu

—

DOI - Digital Object Identifier

—

Jazyk výsledku

angličtina

Název v původním jazyce

Structure and properties of Sb2O3-containing zinc borophosphate glasses

Popis výsledku v původním jazyce

ZnO?B2O3?P2O5 glasses formulated with Sb2O3 were investigated in the series 50ZnO?10B2O3?40P2O5 + xSb2O3 (x = 0?70 mol%). With increasing Sb2O3 content, the values of glass transition temperature decrease from 492 oC down to 394 oC. The dissolution rateof the glasses reveals a maximum for the glass with x = 15 mol% Sb2O3. Raman spectra with increasing Sb2O3 content reflect the depolymerisation of phosphate chains. Antimony at low Sb2O3 content forms individual SbO3 pyramids manifested in the Raman spectra by a broad vibrational band at 520?690 cm-1. In the glasses with a higher Sb2O3 content SbO3 units link into chains and clusters with Sb?O?Sb bridges manifested in the Raman spectra by a strong broad band at 380?520 cm-1. The 31P MAS NMR spectra withincreasing Sb2O3 content reflect the depolymerisation of phosphate chains at low Sb2O3 content and only small changes in the PO4 coordination at a high Sb2O3 content. 11B MAS NMR spectra reveal a steady transformation of B(OP)4 units int

Název v anglickém jazyce

Structure and properties of Sb2O3-containing zinc borophosphate glasses

Popis výsledku anglicky

ZnO?B2O3?P2O5 glasses formulated with Sb2O3 were investigated in the series 50ZnO?10B2O3?40P2O5 + xSb2O3 (x = 0?70 mol%). With increasing Sb2O3 content, the values of glass transition temperature decrease from 492 oC down to 394 oC. The dissolution rateof the glasses reveals a maximum for the glass with x = 15 mol% Sb2O3. Raman spectra with increasing Sb2O3 content reflect the depolymerisation of phosphate chains. Antimony at low Sb2O3 content forms individual SbO3 pyramids manifested in the Raman spectra by a broad vibrational band at 520?690 cm-1. In the glasses with a higher Sb2O3 content SbO3 units link into chains and clusters with Sb?O?Sb bridges manifested in the Raman spectra by a strong broad band at 380?520 cm-1. The 31P MAS NMR spectra withincreasing Sb2O3 content reflect the depolymerisation of phosphate chains at low Sb2O3 content and only small changes in the PO4 coordination at a high Sb2O3 content. 11B MAS NMR spectra reveal a steady transformation of B(OP)4 units int

Druh

J_x - Nezařazeno - Článek v odborném periodiku (Jimp, Jsc a Jost)

CEP obor

JH - Keramika, žáruvzdorné materiály a skla

OECD FORD obor

—

Projekt

<a href="/cs/project/GA104%2F07%2F0315" target="_blank" >GA104/07/0315: Fosfátová a borofosfátová skla dotovaná oxidy těžkých kovů pro optoelektronické a fotonické aplikace.</a><br>

Návaznosti

Z - Vyzkumny zamer (s odkazem do CEZ)

Rok uplatnění

2007

Kód důvěrnosti údajů

S - Úplné a pravdivé údaje o projektu nepodléhají ochraně podle zvláštních právních předpisů

Název periodika

Journal of Non-Crystalline Solids

ISSN

0022-3093

e-ISSN

—

Svazek periodika

2007

Číslo periodika v rámci svazku

353

Stát vydavatele periodika

NL - Nizozemsko

Počet stran výsledku

6

Strana od-do

1828-1833

Kód UT WoS článku

—

EID výsledku v databázi Scopus

—