SbxSe100-x system (0 { x { 8) studied by DSC and Raman spectroscopy.
Identifikátory výsledku
Kód výsledku v IS VaVaI
<a href="https://www.isvavai.cz/riv?ss=detail&h=RIV%2F00216275%3A25310%2F07%3A00006111" target="_blank" >RIV/00216275:25310/07:00006111 - isvavai.cz</a>
Výsledek na webu
—
DOI - Digital Object Identifier
—
Alternativní jazyky
Jazyk výsledku
angličtina
Název v původním jazyce
SbxSe100-x system (0 { x { 8) studied by DSC and Raman spectroscopy.
Popis výsledku v původním jazyce
The SbxSe100-x glass-forming system (x = 0, 1, 2, 4, and 8 at. %) was studied by conventional differential scanning calorimetry (DSC), Step Scan DSC and Raman spectroscopy. Glass transition temperature, Tg, as well as isobaric heat capacity change, deltaCp, were determined. Crystallization of Sb2Se3 from incongruent undercooled melt, followed by trigonal selenium crystallization was observed. The crystallization kinetics of Sb2Se3 was studied in details. Sb2Se3 crystallizes from incongruent melt at Tc =107?2 oC with crystallization enthalpy deltaHc(Sb2Se3) = -52?? J/g. Johnson-Mehl-Avrami kinetics of crystallization with Avrami kinetic exponent close to 3 was found.
Název v anglickém jazyce
SbxSe100-x system (0 { x { 8) studied by DSC and Raman spectroscopy.
Popis výsledku anglicky
The SbxSe100-x glass-forming system (x = 0, 1, 2, 4, and 8 at. %) was studied by conventional differential scanning calorimetry (DSC), Step Scan DSC and Raman spectroscopy. Glass transition temperature, Tg, as well as isobaric heat capacity change, deltaCp, were determined. Crystallization of Sb2Se3 from incongruent undercooled melt, followed by trigonal selenium crystallization was observed. The crystallization kinetics of Sb2Se3 was studied in details. Sb2Se3 crystallizes from incongruent melt at Tc =107?2 oC with crystallization enthalpy deltaHc(Sb2Se3) = -52?? J/g. Johnson-Mehl-Avrami kinetics of crystallization with Avrami kinetic exponent close to 3 was found.
Klasifikace
Druh
J<sub>x</sub> - Nezařazeno - Článek v odborném periodiku (Jimp, Jsc a Jost)
CEP obor
CA - Anorganická chemie
OECD FORD obor
—
Návaznosti výsledku
Projekt
—
Návaznosti
Z - Vyzkumny zamer (s odkazem do CEZ)
Ostatní
Rok uplatnění
2007
Kód důvěrnosti údajů
S - Úplné a pravdivé údaje o projektu nepodléhají ochraně podle zvláštních právních předpisů
Údaje specifické pro druh výsledku
Název periodika
Optoelectronics and Advanced Materials - Rapid Communications
ISSN
1842-6573
e-ISSN
—
Svazek periodika
1
Číslo periodika v rámci svazku
12
Stát vydavatele periodika
RO - Rumunsko
Počet stran výsledku
4
Strana od-do
—
Kód UT WoS článku
000253725600003
EID výsledku v databázi Scopus
—