Utilization of DTA for Two-Step Synthesis of Cu-Mn-Cr Spinel

Popis výsledku v původním jazyce

The novel two-step synthesis method decreasing the calcining temperature necessary for formation of spinel lattice and as well for reaching of bright and clear hue of the pigments prepared were investigated. This work aims to utilization of DTA for synthesis monitoring. Influence of raw materials and temperature of calcination on color properties were observed. The characterization of the samples was performed by X-ray diffraction and colorimetry in the CIE L*a*b* system. It was proved that the black spinel pigment Cu2.3Mn2.8Cr4.9Ox can be prepared at finally temperature 700°C as one-phase system with high quality black hue.

Název v anglickém jazyce

Utilization of DTA for Two-Step Synthesis of Cu-Mn-Cr Spinel

Popis výsledku anglicky

The novel two-step synthesis method decreasing the calcining temperature necessary for formation of spinel lattice and as well for reaching of bright and clear hue of the pigments prepared were investigated. This work aims to utilization of DTA for synthesis monitoring. Influence of raw materials and temperature of calcination on color properties were observed. The characterization of the samples was performed by X-ray diffraction and colorimetry in the CIE L*a*b* system. It was proved that the black spinel pigment Cu2.3Mn2.8Cr4.9Ox can be prepared at finally temperature 700°C as one-phase system with high quality black hue.

Druh

J_x - Nezařazeno - Článek v odborném periodiku (Jimp, Jsc a Jost)

CEP obor

CA - Anorganická chemie

OECD FORD obor

—

Projekt

—

Návaznosti

Z - Vyzkumny zamer (s odkazem do CEZ)

Rok uplatnění

2007

Kód důvěrnosti údajů

S - Úplné a pravdivé údaje o projektu nepodléhají ochraně podle zvláštních právních předpisů

Název periodika

Journal of Thermal Analysis and Calorimetry (Paper)

ISSN

1388-6150

e-ISSN

—

Svazek periodika

88

Číslo periodika v rámci svazku

1

Stát vydavatele periodika

NL - Nizozemsko

Počet stran výsledku

4

Strana od-do

107-110

Kód UT WoS článku

—

EID výsledku v databázi Scopus

—