Srovnání vlivů teploty skelného přechodu a objemové koncentrace pigmentů na antikorozní účinnost pojiv a nátěrových hmot na bázi alkydových a epoxidových pryskyřic

Kód výsledku v IS VaVaI

<a href="https://www.isvavai.cz/riv?ss=detail&h=RIV%2F00216275%3A25310%2F08%3A00007517" target="_blank" >RIV/00216275:25310/08:00007517 - isvavai.cz</a>

Výsledek na webu

—

DOI - Digital Object Identifier

—

Jazyk výsledku

angličtina

Název v původním jazyce

The Comparing of The Effect of Glass Transition Temperature and Pigment Volume Concentration on the Total Anticorrosive Efficiency of Binders, Paints and Anticorrosive Paints Based on Alkyd and Epoxy Resins

Popis výsledku v původním jazyce

This paper presents the results of relationships of glass transition temperatures and pigment volume concentration with respect to anticorrosive protection of binders, paints and anticorrosive paints. The paints and anticorrosive paints were prepared indifferent formulations from two commercial alkyd and epoxy resins, i.e. CHS-ALKYD S 471 X 60, CHS-ALKYD S 622 N 60, and CHS?EPOX 210 X 75, CHS-EPOXY 531 respectively. The pigment volume concentration in the formulations was changed in the range from 10 to 40 vol. %. The corrosion resistance of coatings was measured by accelerated corrosion tests, which were done in two different condensation chambers containing SO2 or water steam + neutral salt spray. The glass transition temperature Tg of paints and anticorrosive paints was measured by differential scanning calorimetry (DSC).

Název v anglickém jazyce

The Comparing of The Effect of Glass Transition Temperature and Pigment Volume Concentration on the Total Anticorrosive Efficiency of Binders, Paints and Anticorrosive Paints Based on Alkyd and Epoxy Resins

Popis výsledku anglicky

This paper presents the results of relationships of glass transition temperatures and pigment volume concentration with respect to anticorrosive protection of binders, paints and anticorrosive paints. The paints and anticorrosive paints were prepared indifferent formulations from two commercial alkyd and epoxy resins, i.e. CHS-ALKYD S 471 X 60, CHS-ALKYD S 622 N 60, and CHS?EPOX 210 X 75, CHS-EPOXY 531 respectively. The pigment volume concentration in the formulations was changed in the range from 10 to 40 vol. %. The corrosion resistance of coatings was measured by accelerated corrosion tests, which were done in two different condensation chambers containing SO2 or water steam + neutral salt spray. The glass transition temperature Tg of paints and anticorrosive paints was measured by differential scanning calorimetry (DSC).

Druh

D - Stať ve sborníku

CEP obor

JK - Koroze a povrchové úpravy materiálu

OECD FORD obor

—

Projekt

<a href="/cs/project/FT-TA2%2F006" target="_blank" >FT-TA2/006: *Nové nátěrové hmoty pro vybrané stavební technologie.</a><br>

Návaznosti

Z - Vyzkumny zamer (s odkazem do CEZ)<br>S - Specificky vyzkum na vysokych skolach

Rok uplatnění

2008

Kód důvěrnosti údajů

S - Úplné a pravdivé údaje o projektu nepodléhají ochraně podle zvláštních právních předpisů

Název statě ve sborníku

Conference Papers of 39th International Conference on Coatings Technology CCT 2008

ISBN

978-80-7395-075-0

ISSN

—

e-ISSN

—

Počet stran výsledku

10

Strana od-do

—

Název nakladatele

Univerzita Pardubice

Místo vydání

Pardubice

Místo konání akce

Seč u Chrudimě

Datum konání akce

28. 5. 2008

Typ akce podle státní příslušnosti

EUR - Evropská akce

Kód UT WoS článku

—