Studium lithno-olovnatých fosfátových a borofosfátových skel.
Identifikátory výsledku
Kód výsledku v IS VaVaI
<a href="https://www.isvavai.cz/riv?ss=detail&h=RIV%2F00216275%3A25310%2F08%3A00007874" target="_blank" >RIV/00216275:25310/08:00007874 - isvavai.cz</a>
Výsledek na webu
—
DOI - Digital Object Identifier
—
Alternativní jazyky
Jazyk výsledku
angličtina
Název v původním jazyce
Study of Lithium-Lead Phosphate and Borophosphate Glasses.
Popis výsledku v původním jazyce
Lithium-lead phosphate and borophosphate glasses were studied in compositional series of xLi2O-(50-x)PbO-50P2O5, xLi2O-(50-x)PbO-10B2O3-40P2O5 and xLi2O-(50-x)PbO-20B2O3-30P2O5. All glasses crystallize on heating within the range of 400-610oC. Their glass transition temperature decreases with increasing Li2O content in the region of x = 0-30 mol% Li2O and then slowly increases in all series of glasses reflecting thus changes in the bond strength of the glass structural network. Density, molar volume andchemical durability of the glasses decrease with increasing Li2O content. The 31P MAS NMR and Raman spectra show that at all glass series with the replacement of PbO by Li2O the ratio of Q2/Q1 units, present in the structure, slightly increase. The 11BMAS NMR spectra of glasses with 10 mol% B2O3 reveal the presence of only BO4 units in the glass structure, whereas the spectra of the glasses with 20 mol% B2O3 reveal also the presence of small amount of BO3 units.
Název v anglickém jazyce
Study of Lithium-Lead Phosphate and Borophosphate Glasses.
Popis výsledku anglicky
Lithium-lead phosphate and borophosphate glasses were studied in compositional series of xLi2O-(50-x)PbO-50P2O5, xLi2O-(50-x)PbO-10B2O3-40P2O5 and xLi2O-(50-x)PbO-20B2O3-30P2O5. All glasses crystallize on heating within the range of 400-610oC. Their glass transition temperature decreases with increasing Li2O content in the region of x = 0-30 mol% Li2O and then slowly increases in all series of glasses reflecting thus changes in the bond strength of the glass structural network. Density, molar volume andchemical durability of the glasses decrease with increasing Li2O content. The 31P MAS NMR and Raman spectra show that at all glass series with the replacement of PbO by Li2O the ratio of Q2/Q1 units, present in the structure, slightly increase. The 11BMAS NMR spectra of glasses with 10 mol% B2O3 reveal the presence of only BO4 units in the glass structure, whereas the spectra of the glasses with 20 mol% B2O3 reveal also the presence of small amount of BO3 units.
Klasifikace
Druh
J<sub>x</sub> - Nezařazeno - Článek v odborném periodiku (Jimp, Jsc a Jost)
CEP obor
JH - Keramika, žáruvzdorné materiály a skla
OECD FORD obor
—
Návaznosti výsledku
Projekt
—
Návaznosti
Z - Vyzkumny zamer (s odkazem do CEZ)
Ostatní
Rok uplatnění
2008
Kód důvěrnosti údajů
S - Úplné a pravdivé údaje o projektu nepodléhají ochraně podle zvláštních právních předpisů
Údaje specifické pro druh výsledku
Název periodika
Advanced Materials Research
ISSN
1022-6680
e-ISSN
—
Svazek periodika
39-40
Číslo periodika v rámci svazku
N
Stát vydavatele periodika
CH - Švýcarská konfederace
Počet stran výsledku
4
Strana od-do
—
Kód UT WoS článku
—
EID výsledku v databázi Scopus
—