Mechanism of degradation of stabilized corrosion resistant steel during the welding cycle

Kód výsledku v IS VaVaI

<a href="https://www.isvavai.cz/riv?ss=detail&h=RIV%2F00216275%3A25310%2F09%3A00008535" target="_blank" >RIV/00216275:25310/09:00008535 - isvavai.cz</a>

Nalezeny alternativní kódy

RIV/00216275:25510/09:00008535

Výsledek na webu

—

DOI - Digital Object Identifier

—

Jazyk výsledku

angličtina

Název v původním jazyce

Mechanism of degradation of stabilized corrosion resistant steel during the welding cycle

Popis výsledku v původním jazyce

The purpose of the presented investigation is to identify destabilisation mechanism of two types of ferritic, corrosion resistant steel caused by the welding cycle. A series of experimental weld joints was made to verify the actual response of non-stabilised corrosion resistant steel and of the same steel stabilised by added titanium. The character and extent of the ensuing structural changes were analysed. Essentials of degradation inside the heat-affected zone were evaluated using optical and scanningelectron microscopy; individual phases were identified by means of EDX microanalysis.

Název v anglickém jazyce

Mechanism of degradation of stabilized corrosion resistant steel during the welding cycle

Popis výsledku anglicky

The purpose of the presented investigation is to identify destabilisation mechanism of two types of ferritic, corrosion resistant steel caused by the welding cycle. A series of experimental weld joints was made to verify the actual response of non-stabilised corrosion resistant steel and of the same steel stabilised by added titanium. The character and extent of the ensuing structural changes were analysed. Essentials of degradation inside the heat-affected zone were evaluated using optical and scanningelectron microscopy; individual phases were identified by means of EDX microanalysis.

Druh

J_x - Nezařazeno - Článek v odborném periodiku (Jimp, Jsc a Jost)

CEP obor

JK - Koroze a povrchové úpravy materiálu

OECD FORD obor

—

Projekt

<a href="/cs/project/1M0519" target="_blank" >1M0519: Výzkumné centrum kolejových vozidel</a><br>

Návaznosti

P - Projekt vyzkumu a vyvoje financovany z verejnych zdroju (s odkazem do CEP)<br>Z - Vyzkumny zamer (s odkazem do CEZ)

Rok uplatnění

2009

Kód důvěrnosti údajů

S - Úplné a pravdivé údaje o projektu nepodléhají ochraně podle zvláštních právních předpisů

Název periodika

Anti-Corrosion Methods and Materials

ISSN

0003-5599

e-ISSN

—

Svazek periodika

54

Číslo periodika v rámci svazku

4

Stát vydavatele periodika

GB - Spojené království Velké Británie a Severního Irska

Počet stran výsledku

12

Strana od-do

—

Kód UT WoS článku

—

EID výsledku v databázi Scopus

—