Transesterification of rapeseed oil by Mg-Al mixed oxides with various Mg/Al molar ratio

Kód výsledku v IS VaVaI

<a href="https://www.isvavai.cz/riv?ss=detail&h=RIV%2F00216275%3A25310%2F15%3A39899401" target="_blank" >RIV/00216275:25310/15:39899401 - isvavai.cz</a>

Výsledek na webu

<a href="http://dx.doi.org/10.1016/j.cej.2014.11.006" target="_blank" >http://dx.doi.org/10.1016/j.cej.2014.11.006</a>

DOI - Digital Object Identifier

<a href="http://dx.doi.org/10.1016/j.cej.2014.11.006" target="_blank" >10.1016/j.cej.2014.11.006</a>

Jazyk výsledku

angličtina

Název v původním jazyce

Transesterification of rapeseed oil by Mg-Al mixed oxides with various Mg/Al molar ratio

Popis výsledku v původním jazyce

Mg-Al mixed oxides with a different Mg/Al molar ratio (from 1.8 to 7.2) were prepared by thermal pre-treatment of hydrotalcite-like precursors at 450 degrees C and used as catalysts for transesterification of rapeseed oil. The goal of the work is to study the influence of Mg/Al molar ratio on the total concentration of basic sites, crystallite size of MgO, specific surface area, yield of ester and leaching of magnesium from the catalyst to liquid products. It was found that the total concentration of basic sites decreases and the crystallite size of MgO, specific surface area and the yield of ester increase with an increasing Mg/Al molar ratio for Mg-Al-Na mixed oxides pre-treated at 450 degrees C. There was observed only negligible magnesium leachingfrom solid Mg-Al mixed oxides to the liquid phases.

Název v anglickém jazyce

Transesterification of rapeseed oil by Mg-Al mixed oxides with various Mg/Al molar ratio

Popis výsledku anglicky

Mg-Al mixed oxides with a different Mg/Al molar ratio (from 1.8 to 7.2) were prepared by thermal pre-treatment of hydrotalcite-like precursors at 450 degrees C and used as catalysts for transesterification of rapeseed oil. The goal of the work is to study the influence of Mg/Al molar ratio on the total concentration of basic sites, crystallite size of MgO, specific surface area, yield of ester and leaching of magnesium from the catalyst to liquid products. It was found that the total concentration of basic sites decreases and the crystallite size of MgO, specific surface area and the yield of ester increase with an increasing Mg/Al molar ratio for Mg-Al-Na mixed oxides pre-treated at 450 degrees C. There was observed only negligible magnesium leachingfrom solid Mg-Al mixed oxides to the liquid phases.

Druh

J_x - Nezařazeno - Článek v odborném periodiku (Jimp, Jsc a Jost)

CEP obor

CF - Fyzikální chemie a teoretická chemie

OECD FORD obor

—

Projekt

<a href="/cs/project/EE2.3.30.0058" target="_blank" >EE2.3.30.0058: Rozvoj kvalitních vědeckovýzkumných týmů na Univerzitě Pardubice</a><br>

Návaznosti

P - Projekt vyzkumu a vyvoje financovany z verejnych zdroju (s odkazem do CEP)

Rok uplatnění

2015

Kód důvěrnosti údajů

S - Úplné a pravdivé údaje o projektu nepodléhají ochraně podle zvláštních právních předpisů

Název periodika

Chemical Engineering Journal

ISSN

1385-8947

e-ISSN

—

Svazek periodika

263

Číslo periodika v rámci svazku

March

Stát vydavatele periodika

CH - Švýcarská konfederace

Počet stran výsledku

8

Strana od-do

160-167

Kód UT WoS článku

000349062900019

EID výsledku v databázi Scopus

—