Fabrication of TiO2 nanotubes on Ti spheres using bipolar electrochemistry
Identifikátory výsledku
Kód výsledku v IS VaVaI
<a href="https://www.isvavai.cz/riv?ss=detail&h=RIV%2F00216275%3A25310%2F20%3A39916396" target="_blank" >RIV/00216275:25310/20:39916396 - isvavai.cz</a>
Nalezeny alternativní kódy
RIV/00216305:26620/20:PU136537
Výsledek na webu
<a href="https://www.sciencedirect.com/science/article/pii/S1388248120300205?via%3Dihub" target="_blank" >https://www.sciencedirect.com/science/article/pii/S1388248120300205?via%3Dihub</a>
DOI - Digital Object Identifier
<a href="http://dx.doi.org/10.1016/j.elecom.2020.106669" target="_blank" >10.1016/j.elecom.2020.106669</a>
Alternativní jazyky
Jazyk výsledku
angličtina
Název v původním jazyce
Fabrication of TiO2 nanotubes on Ti spheres using bipolar electrochemistry
Popis výsledku v původním jazyce
In this work, the anodization of Ti spheres using bipolar electrochemistry is reported for the first time. TiO2 nanotubes were found over the entire surface area of the Ti spheres when a square-wave potential was employed. The TiO2 nanotubes were similar to 77 nm in inner diameter and had a thickness of similar to 2 mu m on the extremities of the Ti spheres. Due to their increased surface area, the Ti spheres covered with TiO2 nanotubes had a rate constant for the photocatalytic degradation of methylene blue which was approximately 2.15 times higher than that of non-anodized Ti spheres with a thin thermal oxide layer.
Název v anglickém jazyce
Fabrication of TiO2 nanotubes on Ti spheres using bipolar electrochemistry
Popis výsledku anglicky
In this work, the anodization of Ti spheres using bipolar electrochemistry is reported for the first time. TiO2 nanotubes were found over the entire surface area of the Ti spheres when a square-wave potential was employed. The TiO2 nanotubes were similar to 77 nm in inner diameter and had a thickness of similar to 2 mu m on the extremities of the Ti spheres. Due to their increased surface area, the Ti spheres covered with TiO2 nanotubes had a rate constant for the photocatalytic degradation of methylene blue which was approximately 2.15 times higher than that of non-anodized Ti spheres with a thin thermal oxide layer.
Klasifikace
Druh
J<sub>imp</sub> - Článek v periodiku v databázi Web of Science
CEP obor
—
OECD FORD obor
21001 - Nano-materials (production and properties)
Návaznosti výsledku
Projekt
Výsledek vznikl pri realizaci vícero projektů. Více informací v záložce Projekty.
Návaznosti
P - Projekt vyzkumu a vyvoje financovany z verejnych zdroju (s odkazem do CEP)
Ostatní
Rok uplatnění
2020
Kód důvěrnosti údajů
S - Úplné a pravdivé údaje o projektu nepodléhají ochraně podle zvláštních právních předpisů
Údaje specifické pro druh výsledku
Název periodika
Electrochemistry Communications
ISSN
1388-2481
e-ISSN
1873-1902
Svazek periodika
111
Číslo periodika v rámci svazku
February
Stát vydavatele periodika
US - Spojené státy americké
Počet stran výsledku
4
Strana od-do
"106669-1"-"106669-4"
Kód UT WoS článku
000512969200018
EID výsledku v databázi Scopus
2-s2.0-85078467243