Stochastic fracture mechanics and size effect

Popis výsledku v původním jazyce

Quasibrittle materials such as concrete, fiber composites, rocks, tough ceramics, sea ice, dry snow slabs, wood and some biomaterials, fail at different nominal strengths with respect to their structural size. Smaller structures fail in a ductile mannerwhich usually involves distributed cracking with strain-softening. The stress redistribution that is caused by fracture and distributed cracking engenders an energetic size effect, i.e., decrease of the nominal strength of structures with increasing st tructure size. A structure far larger than the fracture process zone (FPZ) fails in an almost perfectly brittle manner and, if the failure occurs right at the crack initiation,the failure load is governed by the statistically weakest point in the structure, which gives a basis to the statistical size effect. Strategies for capturing the statistical size effect using the stochastic finite element method in the sense of extreme value statistics are presented. They combine feasible types of M

Název v anglickém jazyce

Stochastic fracture mechanics and size effect

Popis výsledku anglicky

Quasibrittle materials such as concrete, fiber composites, rocks, tough ceramics, sea ice, dry snow slabs, wood and some biomaterials, fail at different nominal strengths with respect to their structural size. Smaller structures fail in a ductile mannerwhich usually involves distributed cracking with strain-softening. The stress redistribution that is caused by fracture and distributed cracking engenders an energetic size effect, i.e., decrease of the nominal strength of structures with increasing st tructure size. A structure far larger than the fracture process zone (FPZ) fails in an almost perfectly brittle manner and, if the failure occurs right at the crack initiation,the failure load is governed by the statistically weakest point in the structure, which gives a basis to the statistical size effect. Strategies for capturing the statistical size effect using the stochastic finite element method in the sense of extreme value statistics are presented. They combine feasible types of M

Druh

V_x - Nezařazeno - Výzkumná zpráva obsahující utajované informace (takový výsledek lze do RIV vložit pouze v případě, že zpráva obsahuje utajované informace a pole R12 = U), nebo souhrnná výzkumná zpráva

CEP obor

JM - Inženýrské stavitelství

OECD FORD obor

—

Projekt

Výsledek vznikl pri realizaci vícero projektů. Více informací v záložce Projekty.

Návaznosti

Z - Vyzkumny zamer (s odkazem do CEZ)

Rok uplatnění

2004

Kód důvěrnosti údajů

S - Úplné a pravdivé údaje o projektu nepodléhají ochraně podle zvláštních právních předpisů

Počet stran výsledku

170

Místo vydání

Brno

Název nakladatele resp. objednatele

VUT v Brně

Verze

—