Citlivostní analýza vlivu počátečních imperfekcí na (i) únosnost a (ii) únavové chování ocelového nosníku
Identifikátory výsledku
Kód výsledku v IS VaVaI
<a href="https://www.isvavai.cz/riv?ss=detail&h=RIV%2F00216305%3A26110%2F04%3APU44931" target="_blank" >RIV/00216305:26110/04:PU44931 - isvavai.cz</a>
Výsledek na webu
—
DOI - Digital Object Identifier
—
Alternativní jazyky
Jazyk výsledku
angličtina
Název v původním jazyce
Sensitivity Analysis of the Effect of Initial Imperfections on the (i) Ultimate Load and (ii) Fatigue behaviour of Steel Plate Girders
Popis výsledku v původním jazyce
The study is divided into two parts: (i) in the first one, the plate girder (Fig. 1) is considered to be exposed to quasi-constant loading (i.e. to loads which are either constant or repeated in a very small number of cycles), while (ii) in the other one, the girder is assumed to be subjected to many times repeated loading.Then it is understandable that the objective of the first part should be to look into the influence of initial imperfections on the static ultimate load of the girder related to the fformation of a plastic failure mechanism in it, while that of the second part was to study the effect of imperfections on the stress state under considerably lesser loads, viz. under such as to correspond to the development of fatigue cracks in the girder and, consequently, to its fatigue limit state. In this case the state of stress was measured by principal surface stresses developing in the crack-prone areas (Fig. 2) of the web ?breathing? under the repeated loads, which ? as was demo
Název v anglickém jazyce
Sensitivity Analysis of the Effect of Initial Imperfections on the (i) Ultimate Load and (ii) Fatigue behaviour of Steel Plate Girders
Popis výsledku anglicky
The study is divided into two parts: (i) in the first one, the plate girder (Fig. 1) is considered to be exposed to quasi-constant loading (i.e. to loads which are either constant or repeated in a very small number of cycles), while (ii) in the other one, the girder is assumed to be subjected to many times repeated loading.Then it is understandable that the objective of the first part should be to look into the influence of initial imperfections on the static ultimate load of the girder related to the fformation of a plastic failure mechanism in it, while that of the second part was to study the effect of imperfections on the stress state under considerably lesser loads, viz. under such as to correspond to the development of fatigue cracks in the girder and, consequently, to its fatigue limit state. In this case the state of stress was measured by principal surface stresses developing in the crack-prone areas (Fig. 2) of the web ?breathing? under the repeated loads, which ? as was demo
Klasifikace
Druh
D - Stať ve sborníku
CEP obor
JN - Stavebnictví
OECD FORD obor
—
Návaznosti výsledku
Projekt
Výsledek vznikl pri realizaci vícero projektů. Více informací v záložce Projekty.
Návaznosti
Z - Vyzkumny zamer (s odkazem do CEZ)
Ostatní
Rok uplatnění
2004
Kód důvěrnosti údajů
S - Úplné a pravdivé údaje o projektu nepodléhají ochraně podle zvláštních právních předpisů
Údaje specifické pro druh výsledku
Název statě ve sborníku
8th Int. Conference Modern Building Materials, Structures and Techniques
ISBN
9986-05-722-1
ISSN
—
e-ISSN
—
Počet stran výsledku
6
Strana od-do
243-248
Název nakladatele
NEUVEDEN
Místo vydání
Vilnius (Lithuania)
Místo konání akce
Vilnius (Lithuania)
Datum konání akce
19. 5. 2004
Typ akce podle státní příslušnosti
EUR - Evropská akce
Kód UT WoS článku
—