Corrosion of galvanized steel in concrete environment and its impact on cement paste microstructure

Popis výsledku v původním jazyce

Corrosion process of galvanized steel in model pore solution of pH 12.5 or 13.5 was studied by means of electrochemical corrosion methods. Saturated solution of Ca(OH)2 causes active corrosion of galvanized steel accompanied with evolution of hydrogen gas. Corrosion resistance of galvanized steel particularly in environment of pH 13.5 is very weak. The microstructure of the interfacial transition zone between hardened Portland cement paste and zinc surface was examined by using porosimetry and SEM methoods. The porosity increases in the range of pores at approx. 10 ?Ým. Cr(III) as well as Cr(VI) based conversion coating reduces the gas evolution in solution of pH 12.5, while in pH 13.5 solution only the Cr(VI) coating is effective.

Název v anglickém jazyce

Corrosion of galvanized steel in concrete environment and its impact on cement paste microstructure

Popis výsledku anglicky

Corrosion process of galvanized steel in model pore solution of pH 12.5 or 13.5 was studied by means of electrochemical corrosion methods. Saturated solution of Ca(OH)2 causes active corrosion of galvanized steel accompanied with evolution of hydrogen gas. Corrosion resistance of galvanized steel particularly in environment of pH 13.5 is very weak. The microstructure of the interfacial transition zone between hardened Portland cement paste and zinc surface was examined by using porosimetry and SEM methoods. The porosity increases in the range of pores at approx. 10 ?Ým. Cr(III) as well as Cr(VI) based conversion coating reduces the gas evolution in solution of pH 12.5, while in pH 13.5 solution only the Cr(VI) coating is effective.

Druh

D - Stať ve sborníku

CEP obor

JN - Stavebnictví

OECD FORD obor

—

Projekt

<a href="/cs/project/GA103%2F02%2F0282" target="_blank" >GA103/02/0282: Korozní odolnost alternativních kovových materiálů pro výztuže betonu</a><br>

Návaznosti

P - Projekt vyzkumu a vyvoje financovany z verejnych zdroju (s odkazem do CEP)

Rok uplatnění

2004

Kód důvěrnosti údajů

S - Úplné a pravdivé údaje o projektu nepodléhají ochraně podle zvláštních právních předpisů

Název statě ve sborníku

Eurocord 2004

ISBN

—

ISSN

—

e-ISSN

—

Počet stran výsledku

9

Strana od-do

1-9

Název nakladatele

Chimie Paris

Místo vydání

Nice

Místo konání akce

Nice

Datum konání akce

9. 9. 2004

Typ akce podle státní příslušnosti

WRD - Celosvětová akce

Kód UT WoS článku

—