Vliv složení a množství draselného aktivátoru na vlastnosti malt z alkalicky aktivované strusky

Kód výsledku v IS VaVaI

<a href="https://www.isvavai.cz/riv?ss=detail&h=RIV%2F00216305%3A26110%2F08%3APU80896" target="_blank" >RIV/00216305:26110/08:PU80896 - isvavai.cz</a>

Výsledek na webu

—

DOI - Digital Object Identifier

—

Jazyk výsledku

angličtina

Název v původním jazyce

Effect of Various Composition and Dosage of Potassium Activator on the Properties of Alkali Activated Slag Mortar

Popis výsledku v původním jazyce

Alkali activated slag is a clinker-free binding material capable of replacing Portland cement in concrete production. In this paper properties of alkali activated blast furnace slag mortars were studied. Potassium silicate and hydroxide solution of various silicate moduli (Sio2/K2O) was used as an activator. Activator dosage was 4, 8, 10 and 20 % with respect to the mass of slag. Compressive strength of the mortar samples was measured 28 days after casting. It was found that increasing amount of activator added to the mixture leads to an increase in compressive strength. No or very little efflorescence was observed on the samples.

Název v anglickém jazyce

Effect of Various Composition and Dosage of Potassium Activator on the Properties of Alkali Activated Slag Mortar

Popis výsledku anglicky

Alkali activated slag is a clinker-free binding material capable of replacing Portland cement in concrete production. In this paper properties of alkali activated blast furnace slag mortars were studied. Potassium silicate and hydroxide solution of various silicate moduli (Sio2/K2O) was used as an activator. Activator dosage was 4, 8, 10 and 20 % with respect to the mass of slag. Compressive strength of the mortar samples was measured 28 days after casting. It was found that increasing amount of activator added to the mixture leads to an increase in compressive strength. No or very little efflorescence was observed on the samples.

Druh

D - Stať ve sborníku

CEP obor

JN - Stavebnictví

OECD FORD obor

—

Projekt

—

Návaznosti

Z - Vyzkumny zamer (s odkazem do CEZ)

Rok uplatnění

2008

Kód důvěrnosti údajů

S - Úplné a pravdivé údaje o projektu nepodléhají ochraně podle zvláštních právních předpisů

Název statě ve sborníku

Junior Scientist Conference 2008

ISBN

978-3-200-01612-5

ISSN

—

e-ISSN

—

Počet stran výsledku

2

Strana od-do

—

Název nakladatele

Vienna University of Technology

Místo vydání

Vienna

Místo konání akce

Vídeň

Datum konání akce

16. 11. 2008

Typ akce podle státní příslušnosti

EUR - Evropská akce

Kód UT WoS článku

—