A refined description of the crack tip stress field in wedge-splitting specimens - a two-parameter fracture mechanics approach

Kód výsledku v IS VaVaI

<a href="https://www.isvavai.cz/riv?ss=detail&h=RIV%2F00216305%3A26110%2F09%3APU86634" target="_blank" >RIV/00216305:26110/09:PU86634 - isvavai.cz</a>

Výsledek na webu

—

DOI - Digital Object Identifier

—

Jazyk výsledku

angličtina

Název v původním jazyce

A refined description of the crack tip stress field in wedge-splitting specimens - a two-parameter fracture mechanics approach

Popis výsledku v původním jazyce

The paper is focused on a detailed numerical analysis of the stress field in specimens used for the wedge splitting test (WST) which is an alternative to the classical fracture tests (bending, tensile) within the fracture mechanics of quasi-brittle building materials, particularly cementitious composites. The near-crack-tip stress field in the WST specimen is described by means of constraint-based two-parameter fracture mechanics in the paper. Different levels of constraint in the vicinity of the cracktip during fracture process through the specimen ligament are characterized by means of the T-stress. Two basic shapes of WST specimen - the cube-shaped and the cylinder-shaped one - are investigated and the determined near-crack-tip stress field parameters are compared to those of compact tension (CT) specimens according to the ASTM standard for classical and round geometry. Particular attention is paid to the effect of the compressive component of the loading force (complementing the s

Název v anglickém jazyce

A refined description of the crack tip stress field in wedge-splitting specimens - a two-parameter fracture mechanics approach

Popis výsledku anglicky

The paper is focused on a detailed numerical analysis of the stress field in specimens used for the wedge splitting test (WST) which is an alternative to the classical fracture tests (bending, tensile) within the fracture mechanics of quasi-brittle building materials, particularly cementitious composites. The near-crack-tip stress field in the WST specimen is described by means of constraint-based two-parameter fracture mechanics in the paper. Different levels of constraint in the vicinity of the cracktip during fracture process through the specimen ligament are characterized by means of the T-stress. Two basic shapes of WST specimen - the cube-shaped and the cylinder-shaped one - are investigated and the determined near-crack-tip stress field parameters are compared to those of compact tension (CT) specimens according to the ASTM standard for classical and round geometry. Particular attention is paid to the effect of the compressive component of the loading force (complementing the s

Druh

J_x - Nezařazeno - Článek v odborném periodiku (Jimp, Jsc a Jost)

CEP obor

JM - Inženýrské stavitelství

OECD FORD obor

—

Projekt

<a href="/cs/project/KJB200410901" target="_blank" >KJB200410901: Lom silikátových kompozitů na vzorcích z jádrových vývrtů ? využití numerického modelování pro pokročilé stanovování lomových parametrů</a><br>

Návaznosti

P - Projekt vyzkumu a vyvoje financovany z verejnych zdroju (s odkazem do CEP)

Rok uplatnění

2009

Kód důvěrnosti údajů

S - Úplné a pravdivé údaje o projektu nepodléhají ochraně podle zvláštních právních předpisů

Název periodika

Applied andComputational Mechanics

ISSN

1802-680X

e-ISSN

—

Svazek periodika

1

Číslo periodika v rámci svazku

4

Stát vydavatele periodika

CZ - Česká republika

Počet stran výsledku

16

Strana od-do

—

Kód UT WoS článku

—

EID výsledku v databázi Scopus

—