Dry pressed ceramic tiles based on fly ash-clay body: influence of fly ash granulometry and pentasodium triphosphate addition
Identifikátory výsledku
Kód výsledku v IS VaVaI
<a href="https://www.isvavai.cz/riv?ss=detail&h=RIV%2F00216305%3A26110%2F10%3APU82958" target="_blank" >RIV/00216305:26110/10:PU82958 - isvavai.cz</a>
Výsledek na webu
—
DOI - Digital Object Identifier
—
Alternativní jazyky
Jazyk výsledku
angličtina
Název v původním jazyce
Dry pressed ceramic tiles based on fly ash-clay body: influence of fly ash granulometry and pentasodium triphosphate addition
Popis výsledku v původním jazyce
Fly ash from brown coal (70 wt.%) and stoneware clay (30 wt.%) were used for the dry pressed ceramic tiles (according to EN 14411) raw materials mixture. The effects of fly ash milling and pentasodium triphosphate addition as a deflocculant and fluxing agent on the properties of green body (flexural strength, bulk density) and fired body (EN ISO 10545 - water absorption, bulk density, true density, apparent porosity, flexural strength, frost resistance) were studied and explained as a function of the firing temperature (1000 - 1150 oC). Fly ash milling (corresponding to 5 wt.% residue of fly ash grains on 0.063 mm sieve) increased the sintering abilities of the fly ash - clay body. A similar effect was achieved by 1.3 wt.% pentasodium triphosphate (PST) addition with an increase in green body flexural strength and a decrease in water content of the granulate. Fly ash-clay bodies can be frost resistant with water absorption above 10 % thanks to positive pore size distribution, which wer
Název v anglickém jazyce
Dry pressed ceramic tiles based on fly ash-clay body: influence of fly ash granulometry and pentasodium triphosphate addition
Popis výsledku anglicky
Fly ash from brown coal (70 wt.%) and stoneware clay (30 wt.%) were used for the dry pressed ceramic tiles (according to EN 14411) raw materials mixture. The effects of fly ash milling and pentasodium triphosphate addition as a deflocculant and fluxing agent on the properties of green body (flexural strength, bulk density) and fired body (EN ISO 10545 - water absorption, bulk density, true density, apparent porosity, flexural strength, frost resistance) were studied and explained as a function of the firing temperature (1000 - 1150 oC). Fly ash milling (corresponding to 5 wt.% residue of fly ash grains on 0.063 mm sieve) increased the sintering abilities of the fly ash - clay body. A similar effect was achieved by 1.3 wt.% pentasodium triphosphate (PST) addition with an increase in green body flexural strength and a decrease in water content of the granulate. Fly ash-clay bodies can be frost resistant with water absorption above 10 % thanks to positive pore size distribution, which wer
Klasifikace
Druh
J<sub>x</sub> - Nezařazeno - Článek v odborném periodiku (Jimp, Jsc a Jost)
CEP obor
JH - Keramika, žáruvzdorné materiály a skla
OECD FORD obor
—
Návaznosti výsledku
Projekt
—
Návaznosti
Z - Vyzkumny zamer (s odkazem do CEZ)
Ostatní
Rok uplatnění
2010
Kód důvěrnosti údajů
S - Úplné a pravdivé údaje o projektu nepodléhají ochraně podle zvláštních právních předpisů
Údaje specifické pro druh výsledku
Název periodika
Ceramics International
ISSN
0272-8842
e-ISSN
—
Svazek periodika
38
Číslo periodika v rámci svazku
1
Stát vydavatele periodika
NL - Nizozemsko
Počet stran výsledku
7
Strana od-do
—
Kód UT WoS článku
—
EID výsledku v databázi Scopus
—