Fracture process analysis in silicate-based composite specimens
Identifikátory výsledku
Kód výsledku v IS VaVaI
<a href="https://www.isvavai.cz/riv?ss=detail&h=RIV%2F00216305%3A26110%2F12%3APU103164" target="_blank" >RIV/00216305:26110/12:PU103164 - isvavai.cz</a>
Výsledek na webu
—
DOI - Digital Object Identifier
—
Alternativní jazyky
Jazyk výsledku
angličtina
Název v původním jazyce
Fracture process analysis in silicate-based composite specimens
Popis výsledku v původním jazyce
Estimation of the size and shape of the zone of material failure developing around the crack tip during fracture of silicate-based composites presents the main focus of the paper. Numerical simulations utilizing two different modelling approaches (lattice-particle type model and finite element model) are used for verification of a semi-analytical technique for the inelastic zone determination developing by the authors. The problem is studied via virtual three-point bending tests on notched beams of twoconsiderably different sizes made of silicate-based materials with three different compositions resulting in significantly dissimilar cohesive behaviour (from quasi-brittle to quasi-ductile/strain hardening). Good agreement between results of the semi-analytical technique for the estimation of the fracture process zone extent and the simulations with discrete model is reported.
Název v anglickém jazyce
Fracture process analysis in silicate-based composite specimens
Popis výsledku anglicky
Estimation of the size and shape of the zone of material failure developing around the crack tip during fracture of silicate-based composites presents the main focus of the paper. Numerical simulations utilizing two different modelling approaches (lattice-particle type model and finite element model) are used for verification of a semi-analytical technique for the inelastic zone determination developing by the authors. The problem is studied via virtual three-point bending tests on notched beams of twoconsiderably different sizes made of silicate-based materials with three different compositions resulting in significantly dissimilar cohesive behaviour (from quasi-brittle to quasi-ductile/strain hardening). Good agreement between results of the semi-analytical technique for the estimation of the fracture process zone extent and the simulations with discrete model is reported.
Klasifikace
Druh
D - Stať ve sborníku
CEP obor
JM - Inženýrské stavitelství
OECD FORD obor
—
Návaznosti výsledku
Projekt
Výsledek vznikl pri realizaci vícero projektů. Více informací v záložce Projekty.
Návaznosti
P - Projekt vyzkumu a vyvoje financovany z verejnych zdroju (s odkazem do CEP)
Ostatní
Rok uplatnění
2012
Kód důvěrnosti údajů
S - Úplné a pravdivé údaje o projektu nepodléhají ochraně podle zvláštních právních předpisů
Údaje specifické pro druh výsledku
Název statě ve sborníku
50th Anual Conference on Experimental Stress Analysis (EAN 2012)
ISBN
978-80-01-05060-6
ISSN
—
e-ISSN
—
Počet stran výsledku
8
Strana od-do
1-8
Název nakladatele
Neuveden
Místo vydání
Tábor, Česká republika
Místo konání akce
Tábor
Datum konání akce
4. 6. 2012
Typ akce podle státní příslušnosti
EUR - Evropská akce
Kód UT WoS článku
—