Fracture process in silicate composite specimens ? X-ray dynamic observation and numerical modelling
Identifikátory výsledku
Kód výsledku v IS VaVaI
<a href="https://www.isvavai.cz/riv?ss=detail&h=RIV%2F00216305%3A26110%2F12%3APU103165" target="_blank" >RIV/00216305:26110/12:PU103165 - isvavai.cz</a>
Nalezeny alternativní kódy
RIV/68378297:_____/12:00384988
Výsledek na webu
—
DOI - Digital Object Identifier
—
Alternativní jazyky
Jazyk výsledku
angličtina
Název v původním jazyce
Fracture process in silicate composite specimens ? X-ray dynamic observation and numerical modelling
Popis výsledku v původním jazyce
Tensile failure in quasi-brittle materials is connected with formation and evolution of what is referred to as the Fracture Process Zone (FPZ) at the tip of propagating crack. Not only the very existence of the material damage area but also its descriptive parameters (volume, shape and energy dissipation distribution) have to be identified in order to validate approaches on both numerical modelling of quasi-brittle behaviour and experimental determination of fracture properties. Radiographic techniquesand Digital Image Correlation method are used in the presented research as being very appropriate for analysing of the FPZ evolution during specimen loading. The experimental results are accompanied with predictions of the FPZ size and shape via semi-analytical technique serving as a part of developing comprehensive method for evaluation of the real fracture-mechanical characteristics of quasi-brittle materials from records of loading tests on laboratory-sized specimens.
Název v anglickém jazyce
Fracture process in silicate composite specimens ? X-ray dynamic observation and numerical modelling
Popis výsledku anglicky
Tensile failure in quasi-brittle materials is connected with formation and evolution of what is referred to as the Fracture Process Zone (FPZ) at the tip of propagating crack. Not only the very existence of the material damage area but also its descriptive parameters (volume, shape and energy dissipation distribution) have to be identified in order to validate approaches on both numerical modelling of quasi-brittle behaviour and experimental determination of fracture properties. Radiographic techniquesand Digital Image Correlation method are used in the presented research as being very appropriate for analysing of the FPZ evolution during specimen loading. The experimental results are accompanied with predictions of the FPZ size and shape via semi-analytical technique serving as a part of developing comprehensive method for evaluation of the real fracture-mechanical characteristics of quasi-brittle materials from records of loading tests on laboratory-sized specimens.
Klasifikace
Druh
D - Stať ve sborníku
CEP obor
JM - Inženýrské stavitelství
OECD FORD obor
—
Návaznosti výsledku
Projekt
<a href="/cs/project/GAP105%2F11%2F1551" target="_blank" >GAP105/11/1551: Energetické a napjatostní aspekty kvazikřehkého lomu ? důsledky pro určování lomově-mechanických parametrů silikátových kompozitů</a><br>
Návaznosti
P - Projekt vyzkumu a vyvoje financovany z verejnych zdroju (s odkazem do CEP)
Ostatní
Rok uplatnění
2012
Kód důvěrnosti údajů
S - Úplné a pravdivé údaje o projektu nepodléhají ochraně podle zvláštních právních předpisů
Údaje specifické pro druh výsledku
Název statě ve sborníku
19th European Conference on Fracture ? Fracture Mechanics for Durability Realiability and Safety (ECF19)
ISBN
978-5-905576-18-8
ISSN
—
e-ISSN
—
Počet stran výsledku
8
Strana od-do
566-573
Název nakladatele
Neuveden
Místo vydání
Kazan, Rusia
Místo konání akce
Kazaň
Datum konání akce
26. 8. 2012
Typ akce podle státní příslušnosti
EUR - Evropská akce
Kód UT WoS článku
—