Physico-mechanical and microstructural properties of rehydrated blended cement pastes
Identifikátory výsledku
Kód výsledku v IS VaVaI
<a href="https://www.isvavai.cz/riv?ss=detail&h=RIV%2F00216305%3A26110%2F14%3APU109184" target="_blank" >RIV/00216305:26110/14:PU109184 - isvavai.cz</a>
Výsledek na webu
—
DOI - Digital Object Identifier
—
Alternativní jazyky
Jazyk výsledku
angličtina
Název v původním jazyce
Physico-mechanical and microstructural properties of rehydrated blended cement pastes
Popis výsledku v původním jazyce
This study aims to investigate the effect of high temperatures of up to 1200 C and rehydration on the mechanical properties, microstructure and phase composition of blended cement pastes prepared from Portland cement (PC), granulated blast furnace slag (GBFS), high-temperature fly ash (FA) and ground limestone (GL). It has been found that the heating process induces a reduction in bulk density, flexural and compressive strength. The proportion of pores with a diameter higher than 0.1 micrometer increases with increasing temperature. The addition of GBFS or FA improves the strength properties of dehydrated cement paste (DCP), but this effect was not observed after rehydration. Cement paste with added GBFS has the best resistivity to high temperatures, but after rehydration, GL cement paste shows better mechanical properties.
Název v anglickém jazyce
Physico-mechanical and microstructural properties of rehydrated blended cement pastes
Popis výsledku anglicky
This study aims to investigate the effect of high temperatures of up to 1200 C and rehydration on the mechanical properties, microstructure and phase composition of blended cement pastes prepared from Portland cement (PC), granulated blast furnace slag (GBFS), high-temperature fly ash (FA) and ground limestone (GL). It has been found that the heating process induces a reduction in bulk density, flexural and compressive strength. The proportion of pores with a diameter higher than 0.1 micrometer increases with increasing temperature. The addition of GBFS or FA improves the strength properties of dehydrated cement paste (DCP), but this effect was not observed after rehydration. Cement paste with added GBFS has the best resistivity to high temperatures, but after rehydration, GL cement paste shows better mechanical properties.
Klasifikace
Druh
J<sub>x</sub> - Nezařazeno - Článek v odborném periodiku (Jimp, Jsc a Jost)
CEP obor
JN - Stavebnictví
OECD FORD obor
—
Návaznosti výsledku
Projekt
<a href="/cs/project/ED2.1.00%2F03.0097" target="_blank" >ED2.1.00/03.0097: AdMaS - Pokročilé stavební materiály, konstrukce a technologie</a><br>
Návaznosti
P - Projekt vyzkumu a vyvoje financovany z verejnych zdroju (s odkazem do CEP)
Ostatní
Rok uplatnění
2014
Kód důvěrnosti údajů
S - Úplné a pravdivé údaje o projektu nepodléhají ochraně podle zvláštních právních předpisů
Údaje specifické pro druh výsledku
Název periodika
Construction and building materials
ISSN
0950-0618
e-ISSN
—
Svazek periodika
2014
Číslo periodika v rámci svazku
54
Stát vydavatele periodika
GB - Spojené království Velké Británie a Severního Irska
Počet stran výsledku
8
Strana od-do
413-420
Kód UT WoS článku
—
EID výsledku v databázi Scopus
—