Enhancing the wood glue bond using cellulose modified epoxy
Identifikátory výsledku
Kód výsledku v IS VaVaI
<a href="https://www.isvavai.cz/riv?ss=detail&h=RIV%2F00216305%3A26110%2F15%3APU117942" target="_blank" >RIV/00216305:26110/15:PU117942 - isvavai.cz</a>
Výsledek na webu
<a href="http://dx.doi.org/10.4028/www.scientific.net/AMR.1122.145" target="_blank" >http://dx.doi.org/10.4028/www.scientific.net/AMR.1122.145</a>
DOI - Digital Object Identifier
<a href="http://dx.doi.org/10.4028/www.scientific.net/AMR.1122.145" target="_blank" >10.4028/www.scientific.net/AMR.1122.145</a>
Alternativní jazyky
Jazyk výsledku
angličtina
Název v původním jazyce
Enhancing the wood glue bond using cellulose modified epoxy
Popis výsledku v původním jazyce
The paper deals with the possibilities of enhancing the durability of wood bonds using the epoxy resin. These types of resin very often failed while exposing the water uptake when wood adherend swells and the bonds failed in bonding interface layer. Using the micro-cellulose fibers in epoxy resin leads to higher fracture toughness while the interphase could better accommodate the large dimensional changes of the wood. That was the reason, why the different amount of micro-ocellulose fibers in epoxy resin were applied and the durability test of single-lap wood joints were performed. The higher percentage of cohesive failure in wood adherend and higher shear strengths after exposing the hygrothermal exposures were achieved
Název v anglickém jazyce
Enhancing the wood glue bond using cellulose modified epoxy
Popis výsledku anglicky
The paper deals with the possibilities of enhancing the durability of wood bonds using the epoxy resin. These types of resin very often failed while exposing the water uptake when wood adherend swells and the bonds failed in bonding interface layer. Using the micro-cellulose fibers in epoxy resin leads to higher fracture toughness while the interphase could better accommodate the large dimensional changes of the wood. That was the reason, why the different amount of micro-ocellulose fibers in epoxy resin were applied and the durability test of single-lap wood joints were performed. The higher percentage of cohesive failure in wood adherend and higher shear strengths after exposing the hygrothermal exposures were achieved
Klasifikace
Druh
J<sub>ost</sub> - Ostatní články v recenzovaných periodicích
CEP obor
—
OECD FORD obor
20101 - Civil engineering
Návaznosti výsledku
Projekt
<a href="/cs/project/LO1408" target="_blank" >LO1408: AdMaS UP - Pokročilé stavební materiály, konstrukce a technologie</a><br>
Návaznosti
P - Projekt vyzkumu a vyvoje financovany z verejnych zdroju (s odkazem do CEP)<br>S - Specificky vyzkum na vysokych skolach
Ostatní
Rok uplatnění
2015
Kód důvěrnosti údajů
S - Úplné a pravdivé údaje o projektu nepodléhají ochraně podle zvláštních právních předpisů
Údaje specifické pro druh výsledku
Název periodika
Advanced Materials Research (online)
ISSN
1022-6680
e-ISSN
1662-8985
Svazek periodika
2015
Číslo periodika v rámci svazku
1122
Stát vydavatele periodika
CH - Švýcarská konfederace
Počet stran výsledku
4
Strana od-do
145-148
Kód UT WoS článku
—
EID výsledku v databázi Scopus
—