Concrete Resistance to Cracking due to Shrinkage
Identifikátory výsledku
Kód výsledku v IS VaVaI
<a href="https://www.isvavai.cz/riv?ss=detail&h=RIV%2F00216305%3A26110%2F16%3APU116301" target="_blank" >RIV/00216305:26110/16:PU116301 - isvavai.cz</a>
Výsledek na webu
<a href="http://dx.doi.org/10.4028/www.scientific.net/SSP.249.96" target="_blank" >http://dx.doi.org/10.4028/www.scientific.net/SSP.249.96</a>
DOI - Digital Object Identifier
<a href="http://dx.doi.org/10.4028/www.scientific.net/SSP.249.96" target="_blank" >10.4028/www.scientific.net/SSP.249.96</a>
Alternativní jazyky
Jazyk výsledku
angličtina
Název v původním jazyce
Concrete Resistance to Cracking due to Shrinkage
Popis výsledku v původním jazyce
This paper suggests an interpretation of the concrete resistance to cracking caused by shrinkage. Cement hydration leads to many chemical processes which cause volume changes and changes of the other physico-mechanical properties of concrete. It is necessary to know the development of residual stresses and corresponding capacity of concrete to establishing of the resistance to shrinkage cracking. Intersection of stress and capacity is a time point which determines that resistance. All necessary concrete properties was established experimentally. The three types of micro-concretes were monitored. On the basis of acquired results it can be stated that the optimal composition of micro-concrete was found because no shrinkage cracks should occur during its life-time.
Název v anglickém jazyce
Concrete Resistance to Cracking due to Shrinkage
Popis výsledku anglicky
This paper suggests an interpretation of the concrete resistance to cracking caused by shrinkage. Cement hydration leads to many chemical processes which cause volume changes and changes of the other physico-mechanical properties of concrete. It is necessary to know the development of residual stresses and corresponding capacity of concrete to establishing of the resistance to shrinkage cracking. Intersection of stress and capacity is a time point which determines that resistance. All necessary concrete properties was established experimentally. The three types of micro-concretes were monitored. On the basis of acquired results it can be stated that the optimal composition of micro-concrete was found because no shrinkage cracks should occur during its life-time.
Klasifikace
Druh
D - Stať ve sborníku
CEP obor
—
OECD FORD obor
20101 - Civil engineering
Návaznosti výsledku
Projekt
Výsledek vznikl pri realizaci vícero projektů. Více informací v záložce Projekty.
Návaznosti
P - Projekt vyzkumu a vyvoje financovany z verejnych zdroju (s odkazem do CEP)
Ostatní
Rok uplatnění
2016
Kód důvěrnosti údajů
S - Úplné a pravdivé údaje o projektu nepodléhají ochraně podle zvláštních právních předpisů
Údaje specifické pro druh výsledku
Název statě ve sborníku
Solid State Phenomena
ISBN
978-3-03835-675-2
ISSN
1662-9779
e-ISSN
—
Počet stran výsledku
6
Strana od-do
96-101
Název nakladatele
Trans Tech Publication
Místo vydání
Switzerland
Místo konání akce
Litomyšl
Datum konání akce
25. 11. 2015
Typ akce podle státní příslušnosti
WRD - Celosvětová akce
Kód UT WoS článku
—