Alkali Activated Binders Based Concrete Specimens: Length Change and Fracture Tests

Kód výsledku v IS VaVaI

<a href="https://www.isvavai.cz/riv?ss=detail&h=RIV%2F00216305%3A26110%2F17%3APU122194" target="_blank" >RIV/00216305:26110/17:PU122194 - isvavai.cz</a>

Výsledek na webu

<a href="http://dx.doi.org/10.4028/www.scientific.net/SSP.258.623" target="_blank" >http://dx.doi.org/10.4028/www.scientific.net/SSP.258.623</a>

DOI - Digital Object Identifier

<a href="http://dx.doi.org/10.4028/www.scientific.net/SSP.258.623" target="_blank" >10.4028/www.scientific.net/SSP.258.623</a>

Jazyk výsledku

angličtina

Název v původním jazyce

Alkali Activated Binders Based Concrete Specimens: Length Change and Fracture Tests

Popis výsledku v původním jazyce

The aim of this paper is to quantify mechanical fracture and length change parameters of the two types of concrete with alkali activated binder. The six beam specimens (75 x 75 x 295 mm) were made from each mixture. After demolding specimens were placed in air storage for 28 days. During this period length change (shrinkage) were recorded in accordance with ASTM C490 (2011). After that the three-point bending test was performed on these specimens with initial stress concentrator at the age of 28 days to obtain the mechanical fracture parameters. Records of fracture tests in form load versus deflection (F–d) diagrams were evaluated using effective crack model and work of fracture method.

Název v anglickém jazyce

Alkali Activated Binders Based Concrete Specimens: Length Change and Fracture Tests

Popis výsledku anglicky

The aim of this paper is to quantify mechanical fracture and length change parameters of the two types of concrete with alkali activated binder. The six beam specimens (75 x 75 x 295 mm) were made from each mixture. After demolding specimens were placed in air storage for 28 days. During this period length change (shrinkage) were recorded in accordance with ASTM C490 (2011). After that the three-point bending test was performed on these specimens with initial stress concentrator at the age of 28 days to obtain the mechanical fracture parameters. Records of fracture tests in form load versus deflection (F–d) diagrams were evaluated using effective crack model and work of fracture method.

Druh

D - Stať ve sborníku

CEP obor

—

OECD FORD obor

20501 - Materials engineering

Projekt

Výsledek vznikl pri realizaci vícero projektů. Více informací v záložce Projekty.

Návaznosti

P - Projekt vyzkumu a vyvoje financovany z verejnych zdroju (s odkazem do CEP)

Rok uplatnění

2017

Kód důvěrnosti údajů

S - Úplné a pravdivé údaje o projektu nepodléhají ochraně podle zvláštních právních předpisů

Název statě ve sborníku

Materials Structure & Micromechnaics of Fracture VIII

ISBN

978-3-03835-626-4

ISSN

1012-0394

e-ISSN

—

Počet stran výsledku

4

Strana od-do

623-626

Název nakladatele

Trans Tech Publications

Místo vydání

Switzerland

Místo konání akce

Brno

Datum konání akce

26. 6. 2016

Typ akce podle státní příslušnosti

WRD - Celosvětová akce

Kód UT WoS článku

—