Fracture properties of concrete specimens made from alkali activated binders.

Kód výsledku v IS VaVaI

<a href="https://www.isvavai.cz/riv?ss=detail&h=RIV%2F00216305%3A26110%2F17%3APU124723" target="_blank" >RIV/00216305:26110/17:PU124723 - isvavai.cz</a>

Výsledek na webu

<a href="http://iopscience.iop.org/article/10.1088/1757-899X/236/1/012068" target="_blank" >http://iopscience.iop.org/article/10.1088/1757-899X/236/1/012068</a>

DOI - Digital Object Identifier

<a href="http://dx.doi.org/10.1088/1757-899X/236/1/012068" target="_blank" >10.1088/1757-899X/236/1/012068</a>

Jazyk výsledku

angličtina

Název v původním jazyce

Fracture properties of concrete specimens made from alkali activated binders.

Popis výsledku v původním jazyce

The aim of this paper is to quantify crack initiation and other fracture properties – effective fracture toughness and specific fracture energy – of two types of concrete with an alkali activated binder. The beam specimens with a stress concentrator were tested in a three-point bending test after 28, 90, and 365 days of maturing. Records of fracture tests in the form of load versus deflection (P–d) diagrams were evaluated using effective crack model and work-of-fracture method and load versus mouth crack opening displacement (P–CMOD) diagrams were evaluated using the Double-K fracture model. The initiation of cracks during the fracture tests for all ages was also monitored by the acoustic emission method. The higher value of monitored mechanical fracture parameters of concrete with alkali activated blast furnace slag were achieved with substitution blast furnace slag by low calcium fly ash in comparison with substitution by cement kiln dust.

Název v anglickém jazyce

Fracture properties of concrete specimens made from alkali activated binders.

Popis výsledku anglicky

The aim of this paper is to quantify crack initiation and other fracture properties – effective fracture toughness and specific fracture energy – of two types of concrete with an alkali activated binder. The beam specimens with a stress concentrator were tested in a three-point bending test after 28, 90, and 365 days of maturing. Records of fracture tests in the form of load versus deflection (P–d) diagrams were evaluated using effective crack model and work-of-fracture method and load versus mouth crack opening displacement (P–CMOD) diagrams were evaluated using the Double-K fracture model. The initiation of cracks during the fracture tests for all ages was also monitored by the acoustic emission method. The higher value of monitored mechanical fracture parameters of concrete with alkali activated blast furnace slag were achieved with substitution blast furnace slag by low calcium fly ash in comparison with substitution by cement kiln dust.

Druh

D - Stať ve sborníku

CEP obor

—

OECD FORD obor

20101 - Civil engineering

Projekt

Výsledek vznikl pri realizaci vícero projektů. Více informací v záložce Projekty.

Návaznosti

P - Projekt vyzkumu a vyvoje financovany z verejnych zdroju (s odkazem do CEP)

Rok uplatnění

2017

Kód důvěrnosti údajů

S - Úplné a pravdivé údaje o projektu nepodléhají ochraně podle zvláštních právních předpisů

Název statě ve sborníku

BESTInfra 2017

ISBN

—

ISSN

1757-899X

e-ISSN

—

Počet stran výsledku

6

Strana od-do

1-6

Název nakladatele

IOP Publishing

Místo vydání

Bristol

Místo konání akce

Praha

Datum konání akce

20. 9. 2017

Typ akce podle státní příslušnosti

WRD - Celosvětová akce

Kód UT WoS článku

000417428700068