Fracture response of alkali-activated slag mortars reinforced by carbon fibres

Kód výsledku v IS VaVaI

<a href="https://www.isvavai.cz/riv?ss=detail&h=RIV%2F00216305%3A26110%2F18%3APU128424" target="_blank" >RIV/00216305:26110/18:PU128424 - isvavai.cz</a>

Výsledek na webu

<a href="http://iopscience.iop.org/article/10.1088/1757-899X/379/1/012027" target="_blank" >http://iopscience.iop.org/article/10.1088/1757-899X/379/1/012027</a>

DOI - Digital Object Identifier

<a href="http://dx.doi.org/10.1088/1757-899X/379/1/012027" target="_blank" >10.1088/1757-899X/379/1/012027</a>

Jazyk výsledku

angličtina

Název v původním jazyce

Fracture response of alkali-activated slag mortars reinforced by carbon fibres

Popis výsledku v původním jazyce

The paper reports a study of the effect of carbon fibres on the mechanical fracture parameters of alkali-activated slag mortars. The carbon fibres were added in the amount of 1, 2 and 3%, respectively with respect to the mass of the slag. The mechanical fracture parameters were determined using evaluation of fracture tests carried out on 40 × 40 × 160 mm beam specimens with an initial central edge notch. The monitored parameters were compressive strength, modulus of elasticity, effective fracture toughness and specific fracture energy. The specimen response during fracture tests was also monitored by means of acoustic emission. It was shown that as the addition of carbon fibres increased the value of compressive strength and modulus of elasticity of alkali-activated slag dropped to 50% in case of the highest amount of fibres. The effective fracture toughness is not significantly influenced by addition of carbon fibres. On the other hand, the fracture energy value gradually increases with addition of carbon fibres, up to more than twofold increase in case of the highest amount of fibres.

Název v anglickém jazyce

Fracture response of alkali-activated slag mortars reinforced by carbon fibres

Popis výsledku anglicky

The paper reports a study of the effect of carbon fibres on the mechanical fracture parameters of alkali-activated slag mortars. The carbon fibres were added in the amount of 1, 2 and 3%, respectively with respect to the mass of the slag. The mechanical fracture parameters were determined using evaluation of fracture tests carried out on 40 × 40 × 160 mm beam specimens with an initial central edge notch. The monitored parameters were compressive strength, modulus of elasticity, effective fracture toughness and specific fracture energy. The specimen response during fracture tests was also monitored by means of acoustic emission. It was shown that as the addition of carbon fibres increased the value of compressive strength and modulus of elasticity of alkali-activated slag dropped to 50% in case of the highest amount of fibres. The effective fracture toughness is not significantly influenced by addition of carbon fibres. On the other hand, the fracture energy value gradually increases with addition of carbon fibres, up to more than twofold increase in case of the highest amount of fibres.

Druh

D - Stať ve sborníku

CEP obor

—

OECD FORD obor

20101 - Civil engineering

Projekt

Výsledek vznikl pri realizaci vícero projektů. Více informací v záložce Projekty.

Návaznosti

P - Projekt vyzkumu a vyvoje financovany z verejnych zdroju (s odkazem do CEP)

Rok uplatnění

2018

Kód důvěrnosti údajů

S - Úplné a pravdivé údaje o projektu nepodléhají ochraně podle zvláštních právních předpisů

Název statě ve sborníku

International Conference Building Materials, Products and Technologies

ISBN

—

ISSN

1757-8981

e-ISSN

—

Počet stran výsledku

6

Strana od-do

1-6

Název nakladatele

IOP Publishing

Místo vydání

Bristol

Místo konání akce

Češkovice

Datum konání akce

29. 5. 2018

Typ akce podle státní příslušnosti

EUR - Evropská akce

Kód UT WoS článku

000478563100027